Method for producing anti-glare film
View Patent ↗A method for producing an anti-glare film includes applying a coating composition including at least a resin, a solvent, and fine particles to a substrate; drying the coating composition applied to the substrate so that a Benard cell structure is formed in the surface of the coating layer due to convection caused during volatilization of the solvent; and curing the resin contained in the coating composition having formed therein a Benard cell structure to form an anti-glare layer having fine irregularities with a moderate surface waviness. The anti-glare layer has a degree of white muddiness of 1.7 or less, as measured by quantitatively determining a diffuse reflection component of the diffused light incident upon the surface of the anti-glare layer.
1. A method for producing an anti-glare film, comprising:
applying a coating composition to a substrate, the coating composition including at least a resin, a solvent, and fine particles;
drying the coating composition applied to the substrate to form a Benard cell structure including randomly spaced irregular agglomerations of the fine particles in a surface of the coating layer by convection caused during volatilization of the solvent; and
curing the resin contained in the coating composition including the formed Benard cell structure to form an anti-glare layer having fine irregularities with a moderate surface waviness,
wherein the anti-glare layer has a dried average coating thickness in the range of from an average particle diameter of the fine particles to three times the average particle diameter of the fine particles.
2. The method according to claim 1 ,
wherein the fine particles are composed mainly of an acryl-styrene copolymer.
3. The method according to claim 1 ,
wherein, in the coating composition drying step, the fine particles are agglomerated mainly in the in-plane direction by the convection caused during volatilization of the solvent.
4. The method according to claim 3 ,
wherein the agglomerated fine particles are covered with the resin in the surface of the anti-glare layer.
5. The method according to claim 1 ,
wherein the resin is an ionizing radiation-curable resin, a thermosetting resin, or a mixed resin thereof and contains at least one of a monomer, an oligomer, and a polymer, which remains in the liquid state after drying the coating composition.
6. The method according to claim 1 ,
wherein, in the resin curing step, the resin is cured by ionizing radiation or heating in such a state that a Benard cell structure is formed in the surface.
7. The method according to claim 1 ,
wherein the fine particles are covered with the resin and do not protrude from a surface of the anti-glare layer.