Thermally stable oleophobic low adhesion coating for inkjet printhead front face
View Patent ↗A coating for an ink jet printhead front face, wherein the coating comprises a oleophobic low adhesion coating. When the oleophobic low adhesion coating is disposed on an ink jet printhead front face surface, jetted drops of ultra-violet gel ink or jetted drops of solid ink exhibit a contact angle greater than 45° and a low sliding angle of less than about 30°. In embodiments, the oleophobic low adhesion coating is thermally stable wherein the surface contact angle and sliding angle show little degradation after the coating is subjected to high temperatures in a range between 180° and 320° or thereabout and high pressures in a range between 100 psi and 400 psi or thereabout during printhead fabrication and manufacturing.
1. A coating for an ink jet printhead front face, wherein the coating comprises:
an oleophobic low adhesion coating, wherein a drop of ultra-violet (UV) gel ink or a drop of solid ink exhibits a sliding angle of less than about 30° with a surface of the coating after the coating has been exposed to a temperature of at least 200° C. for at least 30 minutes.
2. The coating of claim 1 , wherein the sliding angle of less than about 20°.
3. The coating of claim 1 , wherein a drop of UV gel ink or a drop of solid ink exhibits a contact angle of greater than about 45° with the surface of the oleophobic low adhesion coating after the oleophobic low adhesion coating has been exposed to the temperature for at least 30 minutes.
4. The coating of claim 1 , wherein the contact angle is greater than about 55°.
5. The coating of claim 1 , wherein a drop of UV gel ink or a drop of solid ink exhibits a sliding angle of less than 30° with a surface of the oleophobic low adhesion coating and a contact angle of greater than 45° with the surface of the oleophobic low adhesion coating after the coating has been exposed to:
a first curing treatment at a temperature in a range between 130° C. and 150° C. for a period of time in a range between 30 minutes and 2 hours; and
a second curing treatment at a temperature in a range between 250° C. and 330° C. for a period of time in a range between 30 minutes and 2 hours.
6. The coating of claim 1 , wherein a drop of UV gel ink or a drop of solid ink exhibits a sliding angle of less than 30° with a surface of the oleophobic low adhesion coating and a contact angle of greater than 45° with the surface of the oleophobic low adhesion coating after the coating has been soaked in molten solid ink or UV gel ink at a temperature in a range between 120° C. and 150° for 2 days.
7. The coating of claim 1 , wherein a drop of UV gel ink or a drop of solid ink exhibits a sliding angle of less than 30° with a surface of the oleophobic low adhesion coating and a contact angle of greater than 45° with the surface of the oleophobic low adhesion coating after the coating was exposed to the temperature at a pressure of at least 100 psi.
8. The coating of claim 7 , wherein a drop of UV gel ink or a drop of solid ink exhibits a sliding angle of less than 30° with a surface of the oleophobic low adhesion coating and a contact angle of greater than 45° with the surface of the oleophobic low adhesion coating after the coating was exposed to a temperature less than 330° C. at a pressure of less than 400 psi.
9. The coating of claim 1 , wherein the oleophobic low adhesion coating comprises:
a first isocyanate compound; and
a hydroxyl functionalized fluoro-crosslinking material.
10. The coating of claim 9 , wherein the first isocyanate compound is at least one selected from the group consisting of diphenylmethane diisocyanate (MDI), toluene diisocyanate (TDI), hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), hydrogenated MDI, tetra-methyl xylene diisocyanate, naphthalene diisocyanate, cyclohexylene diisocyanate, trimethylhexamethylene diisocyanate, bis(4-isocyanatocyclohexyl) methane, uretidione dimers of monomeric diisocynates of one or more of HDI, IPDI, TDI and MDI, cyclotrimerized isocyanurates of monomeric diisocynates of one or more of HDI, IPDI and TDI, suitable oligomers, polymers or copolymers containing isocyanate (—NCO) functional groups, and a mixture thereof.
11. The coating of claim 9 , wherein the hydroxyl functionalized fluoro-crosslinking material comprises at least one dihydroxy perfluoropolyether compound.
12. The coating of claim 9 , wherein the oleophobic low adhesion coating further comprises a second isocyanate compound different from the first isocyanate compound.
13. The coating of claim 12 , wherein the second isocyanate compound is at least one selected from the group consisting of diphenylmethane diisocyanate (MDI), toluene diisocyanate (TDI), hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), hydrogenated MDI, tetra-methyl xylene diisocyanate, naphthalene diisocyanate, cyclohexylene diisocyanate, trimethylhexamethylene diisocyanate, bis(4-isocyanatocyclohexyl) methane, uretidione dimers of monomeric diisocynates of one or more of HDI, IPDI, TDI and MDI, cyclotrimerized isocyanurate of monomeric diisocynates of one of more of HDI, IPDI and TDI, suitable oligomers, polymers or copolymers containing isocyanate (—NCO) functional groups, and a mixture thereof.
14. A process of forming an oleophobic low adhesion coating for an ink jet printhead front face, comprising:
coating a reactant mixture comprising a first isocyanate compound and a hydroxyl functionalized fluoro-crosslinking material onto a substrate;
subjecting the coated reactant mixture to a first curing treatment at a first temperature; and
thereafter, subjecting the coated reactant mixture to a second curing treatment at a second temperature higher than the first temperature.
15. The process of claim 14 , wherein the hydroxyl functionalized fluoro-crosslinking material is present within the reactant mixture in a range between about 30% by weight to about 90% by weight.
16. The process of claim 14 , wherein the first temperature is 130° C.
17. The process of claim 16 , wherein the second temperature is 290° C.
18. An oleophobic low adhesion coating for an ink jet printhead front face formed according to the process of claim 14 , wherein a drop of ultra-violet (UV) gel ink or a drop of solid ink exhibits a sliding angle of less than about 30° with a surface of the oleophobic low adhesion coating and exhibits a contact angle of greater than about 45° with the surface of the oleophobic low adhesion coating after the coating has been exposed to a temperature of at least 200° C. for at least 30 minutes.