Aqueous dispersion, its production method, and its use

1. A method for producing an aqueous dispersion comprising:

melt kneading (A) at least one thermoplastic resin, wherein thermoplastic resin is (i) an interpolymer of ethylene with at least one comonomer selected from the group consisting of a C4-C20 linear, branched or cyclic diene, and a compound represented by the formula H2C═CHR wherein R is a C1-C20 linear, branched or cyclic alkyl group or a C6-C20 aryl group; or (ii) an interpolymer of propylene with at least one comonomer selected from the group consisting of ethylene, a C4-C20 linear, branched or cyclic diene, and a compound represented by the formula H2C═CHR wherein R is a C1-C20 linear, branched or cyclic alkyl group or a C6-C20 aryl group and (B) at least one dispersing agent; and (C) in the presence of water and optionally a basic substance in an extruder;

thereby forming an emulsified mixture comprising from 1 to 3% by weight of water;

contacting said emulsified mixture with additional water in said extruder and while optionally removing heat from said emulsified mixture;

thereby forming solid particles dispersed in water; and

thereby producing said aqueous dispersion, wherein said dispersions has an average volume particle size in the range of from 0.05 to 5 μm, a pH in the range of 8 to 11.

2. The method according to claim 1 , wherein the dispersing agent comprises less than about 4 percent by weight based on the weight of the thermoplastic resin.

3. The method according to claim 1 , wherein the interpolymer of propylene is a propylene-rich alpha-olefin interpolymer comprising 5 to 25% by weight of ethylene-derived units and 95 to 75% by weight of propylene-derived units, the copolymer having:

(a) a melting point of less than 90 C;

(b) a relationship of elasticity to 500% tensile modulus such that the elasticity is less than or equal to 0.935M+12, where elasticity is in percent and M is the 500% tensile modulus in MPa; and

(c) a relationship of flexural modulus to 500% tensile modulus such that flexural modulus is less than or equal to 4.2e0.27M+50, where flexural modulus is in MPa and M is the 500% tensile modulus in MPa.

4. The method according to claim 1 , wherein the interpolymer of propylene is a propylene-rich alpha-olefin interpolymer comprising units derived from propylene and at least one comonomer selected from the group consisting of ethylene and C4 to C20 alpha-olefins, having a propylene content of greater than 65 mole percent a weight average molecular weight (Mw) of from about 15,000 to about 200,000, a weight average molecular weight/number average molecular weight ratio (Mw/Mn) of from about 1.5 to about 4, and a heat of fusion of from about 30 to about 80 J/g as determined by DSC.

5. The method according to claim 1 , wherein the interpolymer of ethylene has a density of less than about 0.92 g/cc.

6. The method according to claim 1 , wherein the propylene ethylene interpolymer has an ethylene content of about 5% to about 25% by weight.

7. The method according to claim 1 , wherein the at least one thermoplastic resin has a crystallinity of less than about 50%.

8. The method according to claim 1 , wherein the dispersing agent comprises at least one carboxylic acid, at least one salt of at least one carboxylic acid, at least one carboxylic acid ester, or at least one salt of at least one carboxylic acid ester.

9. The method according to claim 1 , wherein the dispersing agent has fewer than 25 carbon atoms.

10. The method according to claim 1 , wherein the dispersing agent is selected from the group consisting of ethylene carboxylic acid copolymers.

11. The method according to claim 1 , wherein the dispersing agent is an ethylene acrylic acid copolymer or an ethylene methacrylic acid copolymer.

12. The method of claim 1 , wherein the dispersion has a particle size distribution defined as volume average particle diameter (Dv) divided by number average particle diameter (Dn) of less than or equal to about 2.0.