View Patent ↗The object of the invention is a method for producing polyurethane and/or polyisocyanurate insulating foam based on foaming reaction mixtures containing polyisocyanates, compounds having reactive hydrogen atoms, propellants, stabilizers, nucleation agents, and optionally further additives, which is characterized in that porous solids, in particular silicates having a zeolite structure, are used as the nucleation agents.
1. A process for producing polyurethane and polyisocyanurate insulation foams based on foamable reaction mixtures containing polyisocyanates, compounds having reactive hydrogen atoms, blowing agents, stabilizers, nucleating agents and, if appropriate, further additives, the process comprising:
utilizing porous solids having a zeolite structure as nucleating agents in an amount of 0.2 to 1.5 parts by weight zeolite per 100 parts by weight polyol;
wherein the insulation foams produced have a density of from 25 kg/m 3 to 45 kg/m 3 ; and
wherein the insulation foams produced have a number of cells per centimetre is in the range of greater than 40 cells/cm.
2. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 1 ;
wherein porous silica, microporous and/or mesoporous silica gels, microporous and/or mesoporous silicates or aluminosilicates are used as nucleating agents having a zeolite structure.
3. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 2 ;
wherein FAU zeolites are used as nucleating agents.
4. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 2 ;
wherein LTA zeolites are used as nucleating agents.
5. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 2 ;
wherein MFI zeolites are used as nucleating agents.
6. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 2 ;
wherein MOR zeolites are used as nucleating agents.
7. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 2 ;
wherein GIS zeolites are used as nucleating agents.
8. The process for producing polyurethane or polyisocyanurate insulation foams according to claim 2 ;
wherein the porous solids, before being utilized as nucleating agents, are pretreated by filling the pores in a targeted manner.
9. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 8 ;
wherein, in the pretreatment, the pores of the porous solids are filled with fluorine-containing organic compounds.
10. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 9 ;
wherein, in the pretreatment, the pores of the porous solids are filled with fluorinated hydrocarbons and/or perfluoroalkanes.
11. A polyurethane or polyisocyanurate insulation foam produced according to claim 1 .
12. The polyurethane or polyisocyanurate insulation foam according to claim 11 ;
wherein the polyurethane and polyisocyanurate insulation foams have a thermal conductivity of less than or equal to 22.4 mW/m*K.
13. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 1 ;
wherein methylendiphenyl diisocyanate MDI is used as isocyanate component.
14. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 10 ;
wherein methylendiphenyl diisocyanate MDI is used as isocyanate component.
15. The process for producing polyurethane and polyiscyanurate insulation foams according to claim 1 ;
wherein the insulation foams produced have a thermal conductivity of no more than 22.4 mW/m*K.
16. A polyurethane or polyisocyanurate insulation foam produced according to claim 9 .
17. The process for producing polyurethane and polyisocyanurate insulation foams according to claim 9 ;
wherein the porous solids pretreated and utilized as nucleating agents are zeolite X.