Vulcanized rubber laminate
View Patent ↗Disclosed is a vulcanized rubber laminate in which both an unvulcanized epichlorohydrin-based rubber composition layer containing a specific polyfunctional (meth)acrylate compound and a specific vulcanizing agent and an unvulcanized fluororubber composition layer containing a specific vulcanizing agent are heated and bonded, whereby, both rubber layers are firmly bonded. A vulcanized rubber laminate in which (A) an unvulcanized epichlorohydrin-based rubber composition layer and (B) an unvulcanized fluororubber composition layer are heated and bonded, wherein the unvulcanized epichlorohydrin-based rubber composition (A) contains: (1) a polyfunctional (meth)acrylate compound having two or more (meth) acryloyl groups in the molecule, and (2) at least one kind selected from the group consisting of a triazine-based vulcanizing agent, a thiourea-based vulcanizing agent, a quinoxaline-based vulcanizing agent and a bisphenol-based vulcanizing agent, and the unvulcanized fluororubber composition (B) contains an organic peroxide-based vulcanizing agent.
1. A vulcanized rubber laminate in which (A) an unvulcanized epichlorohydrin-based rubber composition layer and (B) an unvulcanized fluororubber composition layer are heated and bonded, wherein
the unvulcanized epichlorohydrin-based rubber composition (A) contains:
(1) a polyfunctional (meth)acrylate compound having two or more (meth)acryloyl groups in the molecule, the amount of said polyfunctional (meth)acrylate compound is 1 to 15 parts by weight relative to 100 parts by weight of the epichlorohydrin-based rubber, and
(2) at least one kind selected from the group consisting of a triazine-based vulcanizing agent, a thiourea-based vulcanizing agent, a quinoxaline-based vulcanizing agent and a bisphenol-based vulcanizing agent, and
the unvulcanized fluororubber composition (B) contains an organic peroxide-based vulcanizing agent.
2. The vulcanized rubber laminate according to claim 1 , wherein the unvulcanized epichlorohydrin-based rubber composition (A) further contains (3) a compound of a salt of copper.
3. The vulcanized rubber laminate according to claim 2 , wherein the compound of a salt of copper (3) is a copper salt of carboxylic acid and/or a copper salt of dithiocarbamic acid.
4. The vulcanized rubber laminate according to claim 1 , wherein the polyfunctional (meth)acrylate compound (1) has three or more (meth)acryloyl groups in the molecule.
5. The vulcanized rubber laminate according to claim 1 , wherein the triazine-based vulcanizing agent is 2,4,6-trimercapto-s-triazine.
6. The vulcanized rubber laminate according to claim 1 , wherein the thiourea-based vulcanizing agent is 2-mercaptoimidazoline (ethylene thiourea).
7. The vulcanized rubber laminate according to claim 1 , wherein the quinoxaline-based vulcanizing agent is 6-methylquinoxaline-2,3-dithiocarbonate.
8. The vulcanized rubber laminate according to claim 1 , wherein the bisphenol-based vulcanizing agent is bisphenol AF and/or bisphenol S.
9. The vulcanized rubber laminate according to claim 1 , wherein a fluororubber of the unvulcanized fluororubber composition (B) contains a copolymer of vinylidene fluoride and other copolymerizable fluorine-containing olefin, and
the fluorine-containing olefin is at least one kind selected from the group consisting of hexafluoropropene, pentafluoropropene, trifluoroethylene, trifluorochloroethylene, tetrafluoroethylene, vinyl fluoride, perfluoromethyl vinyl ether and perfluoropropyl vinyl ether.