Silicone resin, process for producing the same, and curable resin composition comprising the same
View Patent ↗Provided are a silicone resin that yields a cured product excellent in flexibility, toughness, and heat resistance and high in transparency, a process for producing the said silicone resin, and a curable resin composition comprising the said silicone resin. The silicone resin is obtained by reacting an organopolysiloxane containing SiH groups represented by general formula (3) with an organopolysiloxane containing hydroxyl groups at both ends represented by general formula (5) and an alcohol containing radically reactive groups represented by general formula (6) in the presence of a hydroxylamine compound represented by general formula (4) as a catalyst and this silicone resin is used in formulating a curable resin composition. In the general formulas, R is an alkyl group of 1-12 carbon atoms optionally containing an oxygen atom or an aryl group, R 1 is an alkyl group, Y is a hydrocarbon group of 1-12 carbon atoms optionally containing an oxygen atom, Z is a (meth)acryloyl group, a vinyl group, or an allyl group, and n, s, m, and r are numbers respectively expressed as 0<n≦2,000, 0<s≦100, 0<m≦1,000, and 1<r≦6.
1. A silicone resin containing radically reactive groups represented by the following general formula (1):
wherein R is an alkyl group of 1-12 carbon atoms optionally containing an oxygen atom or an aryl group, 0<1≦100, 0<m≦1,000, 0<n≦2,000, 0<o<100−l, p≧0, q≦100−l−o, and X is a monovalent group containing at least 1 unsaturated linkage represented by the following general formula (2);
X: —O(Y)(Z) r (2)
wherein Y is a hydrocarbon group of 1-12 carbon atoms optionally containing an oxygen atom, Z is a (meth)acryloyl group, a vinyl group, or an allyl group, and r is a number expressed as 1≦r≦6;
wherein the silicone resin is produced by a process comprising reacting an organopolysiloxane containing SiH groups represented by the following general formula (3)
wherein R is an alkyl group of 1-12 carbon atoms optionally containing an oxygen atom or an aryl group, and s and m are numbers respectively expressed as 0<s≦100 and 0<m≦1,000, in the presence of a hydroxylamine compound represented by the following general formula (4)
HONR 1 2 (4)
wherein R 1 is an alkyl group with an organopolysiloxane containing hydroxyl groups at both ends represented by the following general formula (5)
wherein R is an alkyl group of 1-12 carbon atoms optionally containing an oxygen atom or an aryl group, and n is a number expressed as 0<n≦2,000, and with an alcohol containing radically reactive groups represented by the following general formula (6)
HO(Y)(Z) r (6)
wherein Y is a hydrocarbon group of 1-12 carbon atoms optionally containing oxygen atom, Z is a (meth)acryloyl group, a vinyl group, or an allyl group, and r is a number expressed as 1≦r≦6.
2. A curable resin composition comprising the curable silicone resin of claim 1 and a radical polymerization initiator.
3. A molded silicone resin article obtained by radical copolymerization of the curable resin composition described in claim 2 .
4. A molded silicone resin article as described in claim 3 which satisfies the following conditions (i) to (iv):
(i) modulus of elasticity at 25° C.: 0.01-1,000 MPa
(ii) elongation at distance between chucks, 25-50 mm, test speed, 5-50 mm/min: 10-50%
(iii) light transmission at 550 nm: 88-94%
(iv) coefficient of liner thermal expansion: 100-1,000 ppm/K.