Epoxidized soyate diesters and methods of using same
View Patent ↗An unhindered polyol is used to react with an epoxidized soyate to make epoxidized soyate diester in the presence of a catalyst. The unhindered polyol can be 1,3-propanediol or any polyol having four or more carbon atoms with no two adjacent carbon atoms having hydroxyl functionality. Preferably, a combination of catalysts is used to promote the transesterification reaction of the epoxidized soyate with the unhindered polyol to yield a high percentage of epoxidized soyate diester with epoxy functionality retained. The primary catalyst is a metallic hydroxide, and the secondary catalyst is a titanate. Bioderived epoxidized soyate diester plasticizers useful for thermoplastics and thermosets result.
1. A method of making an epoxidized soyate diester, comprising the step of mixing under heat and agitation
(a) epoxidized soyate;
(b) unhindered polyol; and
(c) a catalyst
to make an epoxidized soyate diester.
2. The method of claim 1 , wherein the unhindered polyol is selected from the group consisting of 1,3-propanediol, 2-methyl-1,3-propanediol, 2,2′-dimethyl-1,3-propanediol, 1,3-butanediol, 1,4-butanediol, 2-methyl-1,4-butanediol, 1,5-pentanediol, 2-methyl-2,4-pentanediol, 3-methyl-1,5-pentanediol, 1,3-hexanediol, 1-4-hexanediol, 1,5-hexanediol, 1,6-hexanediol, 2,2′-dihydroxypropyl ether, diethylene glycol, dipropylene glycol, triethylene glycol, and combinations thereof.
3. The method of claim 1 , wherein the catalyst is a catalyst system, comprising:
(a) a primary catalyst comprising a metallic hydroxide and
(b) a secondary catalyst comprising a titanate.
4. The method of claim 3 , wherein the primary catalyst is a metallic hydroxide flake dissolved in alcohol for further processing.
5. The method of claim 3 , wherein the metallic hydroxide is an alkali metal hydroxide or an alkaline metal earth hydroxide.
6. The method of claim 5 , wherein the metallic hydroxide is potassium hydroxide.
7. The method of claim 5 , wherein the secondary catalyst is selected from the group consisting of 2-ethylhexyl titanate, tetraisopropyl titanate, tetrabutyl titanate, tetrakis-2-ethylhexyl titanate, and combinations thereof.
8. The method of claim 7 , wherein the secondary catalyst is tetrakis-2-ethylhexyl titanate.
9. The method of claim 3 , wherein the epoxidized soyate monoester is selected from the group consisting of epoxidized methyl soyate, epoxidized ethyl soyate, epoxidized butyl soyate, epoxidized octyl soyate, and combinations thereof.
10. The method of claim 9 , wherein the epoxidized soyate monoester has from about 0.5 to about 4 epoxy groups per molecule.
11. The method of claim 9 , wherein the epoxidized soyate is epoxidized methyl soyate and the polyol is 1,3-propanediol and wherein the resulting product of reaction is epoxidized 1,3-propanediol disoyate.
12. The method of claim 3 , wherein the molar ratio of the polyol, the metallic hydroxide, the titanate, and the optional alcohol solvent relative to the epoxidized soyate ranges according to the following table:
Epoxidized soyate
1.0
Unhindered Polyol
0.2-0.5
Metallic hydroxide
0.01-0.02
Titanate
0.007-0.015
Optional alcohol solvent
0-0.22
13. An epoxidized soyate diester selected from the group consisting of epoxidized 1,3-propanediol disoyate, epoxidized 2-methyl-1,3-propanediol disoyate, epoxidized 2,2′-dimethyl-1,3-propanediol disoyate, epoxidized 1,3-butanediol disoyate, epoxidized 1,4-butanediol disoyate, epoxidized 2-methyl-1,4-butanediol disoyate, epoxidized 1,5-pentanediol disoyate, epoxidized 2-methyl-2,4-pentanediol disoyate, epoxidized 3-methyl-1,5-pentanediol disoyate, epoxidized 1,3-hexanediol disoyate, epoxidized 1-4-hexanediol disoyate, epoxidized 1,5-hexanediol disoyate, epoxidized 1,6-hexanediol disoyate, epoxidized 2,2′-dihydroxypropyl ether disoyate, epoxidized diethylene glycol disoyate, epoxidized dipropylene glycol disoyate, epoxidized triethylene glycol disoyate, and combinations thereof.
14. A method of using the epoxidized soyate diester of claim 13 , comprising the step of mixing the diester with a thermoplastic or thermoset polymer to form a plasticized polymer compound.
15. The method of claim 14 , wherein the polymer is polyvinyl chloride in the form of a flexible solid.
16. The method of claim 14 , wherein the polymer is polyvinyl chloride in the form of a plastisol.
17. A flexible polymer compound, comprising:
(a) 40-90 weight percent of polymer and
(b) 10-60 weight percent an epoxidized soyate diester of claim 13 .
18. A plastisol, comprising:
(a) 10-90 weight percent of thermoplastic polymer and
(b) 10-90 weight percent of an epoxidized soyate diester of claim 13 .