Mixed metal olivine electrode materials for lithium ion batteries having improved specific capacity and energy density
View Patent ↗Improved positive electrode material and methods for making the same are described. Lithium-iron-manganese phosphate materials, doped with one or more dopant Co, Ni, V, and Nb, and methods for making the same are described. The improved positive electrode material of the present invention is capable of exhibiting improved energy density and/or specific capacity for use in wide range of applications. In certain embodiments, energy density of greater than 340 mWh/g is possible.
1. A positive electrode material, comprising:
an electroactive material having an overall composition comprising lithium (Li), iron (Fe), manganese (Mn), one or more dopants (D), and phosphate (PO 4 ), wherein the amount of Fe+Mn+D=1.0;
a ratio of an amount of Li:(Fe+Mn+D) ranges from greater than 1.0 to 1.05;
a ratio of an amount of PO 4 :(Fe+Mn+D) ranges from greater than 1.0 to 1.025;
D is one or more dopants each selected from the group consisting of cobalt (Co), nickel (Ni), vanadium (V), and niobium (Nb);
an element amount of Mn ranges from 0.35 to 0.60;
an amount of D ranges from about 0.001 to about 0.10; and
the electroactive material comprises at least one phase having an olivine structure comprising said Li, Fe, Mn, D, and phosphate; and
wherein the combination of the excess lithium with the amount of Mn has an energy density of at least 250 mWh/g and a specific capacity of at least 100 mAh/g at a 20C discharge rate during operation in a battery cell of the electroactive material.
2. The positive electrode material as claimed in claim 1 , wherein the positive electrode material is capable of providing an energy density of at least 340 m Wh/g at 20C discharge rate during operation in a battery cell.
3. The positive electrode material as claimed in claim 1 , said electroactive material further comprising fluorine substituted at a phosphate lattice site.
4. The positive electrode material as claimed in claim 1 , wherein D comprises at least one dopant comprising Co at an amount of up to about 0.05.
5. The positive electrode material as claimed in claim 1 , wherein D comprises at least one dopant comprising Co at an amount of up to about 0.03.
6. The positive electrode material as claimed in claim 1 , wherein D comprises more than one dopants comprising an amount of Co up to about 0.05 and an amount of Ni up to about 0.035.
7. The positive electrode material as claimed in claim 1 , wherein D comprises more than one dopants comprising an amount of Co up to about 0.02 and an amount of Ni up to about 0.02.
8. The positive electrode material as claimed in claim 1 , wherein D comprises more than one dopants comprising an amount of Co up to about 0.05, an amount of Ni up to about 0.035, and an amount of V up to about 0.05.
9. The positive electrode material as claimed in claim 1 , wherein D comprises more than one dopants comprising an amount of Co up to about 0.02, an amount of Ni up to about 0.02, and an amount of V up to about 0.04.
10. The positive electrode material as claimed in claim 1 , wherein the electroactive material comprises an amount of Co up to about 0.05, an amount of Ni up to about 0.035, an amount of V up to about 0.05, and an amount of F up to about 0.06.
11. The positive electrode material as claimed in claim 1 , wherein the electroactive material comprises an amount of Co up to about 0.02, an amount of Ni up to about 0.02, an amount of V up to about 0.04, and an amount of F up to about 0.025.
12. The positive electrode material as claimed in claim 1 , wherein the positive electrode material is one or more electroactive materials selected from the group consisting of
Li 1.050 Mn 0.450 Fe 0.500 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.025 ,
Li 1.040 Mn 0.400 Fe 0.560 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.040 Mn 0.450 Fe 0.520 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.030 Mn 0.450 Fe 0.520 Co 0.010 Ni 0.010 V 0.010 (PO 4 ) 1.005 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.010 F 0.015 ,
Li 1.050 Mn 0.450 Fe 0.510 Co 0.0100 Ni 0.005 V 0.025 (PO 4 ) 1.020 ,
Li 1.050 Mn 0.450 Fe 0.500 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.025 ,
Li 1.040 Mn 0.400 Fe 0.560 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.030 Mn 0.450 Fe 0.520 Co 0.010 Ni 0.010 V 0.010 (PO 4 ) 1.005 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.010 F 0.015 , and
Li 1.050 Mn 0.450 Fe 0.510 Co 0.0100 Ni 0.005 V 0.025 (PO 4 ) 1.020 .
13. The positive electrode material as claimed in claim 1 , wherein the positive electrode material is one or more electroactive materials selected from the group consisting of
Li 1.050 Mn 0.450 Fe 0.500 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.025 ,
Li 1.040 Mn 0.400 Fe 0.560 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.010 F 0.015 ,
Li 1.050 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.025 V 0.025 (PO 4 ) 1.020 ,
Li 1.050 Mn 0.450 Fe 0.500 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.025 ,
Li 1.040 Mn 0.400 Fe 0.560 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.020 (PO 4 ) 1.015 ,
Li 1.040 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.010 V 0.030 (PO 4 ) 1.010 F 0.015 , and
Li 1.050 Mn 0.450 Fe 0.510 Co 0.010 Ni 0.005 V 0.025 (PO 4 ) 1.020 .
14. The positive electrode material as claimed in claim 1 , wherein the positive electrode material consists essentially of an olivinic phase.
15. The positive electrode material as claimed in claim 1 , wherein the positive electrode material consists essentially of an olivinic phase and dopant-rich secondary phases.
16. The positive electrode material as claimed in claim 1 , wherein the positive electrode material is capable of providing an energy density of at least 340 m Wh/g and a specific capacity of at least 110 mAh/g at 20C discharge rate during operation in a battery cell.
17. The positive electrode material as claimed in claim 1 , wherein the positive electrode material is capable of providing an energy density of at least 400 m Wh/g and a specific capacity of at least 125 mAh/g at 20C discharge rate during operation in a battery cell.
18. The positive electrode material as claimed in claim 1 , wherein D is one or more dopants wherein each dopant is selected from the group consisting of cobalt (Co), vanadium (V), and niobium (Nb).
19. The positive electrode material as claimed in claim 1 , wherein D is one or more dopants wherein each dopant is selected from the group consisting of cobalt (Co) and vanadium (V).
20. A positive electrode comprising the positive electrode material of claim 1 .
21. The positive electrode as claimed in claim 20 , further comprising fluorine.
22. The positive electrode as claimed in claim 20 , wherein the positive electrode material is capable of providing an energy density of at least 340 m Whig and a specific capacity of at least 110 mAh/g at 20C discharge rate during operation in a battery cell.
23. The positive electrode as claimed in claim 20 , wherein D is one or more dopants wherein each dopant is selected from the group consisting of cobalt (Co), vanadium (V), and niobium (Nb).
24. The positive electrode as claimed in claim 20 , wherein D is one or more dopants wherein each dopant is selected from the group consisting of cobalt (Co) and vanadium (V).
25. A lithium secondary cell, comprising:
a positive electrode in electrical contact with a positive electrode current collector, said current collector in electrical connection with an external circuit;
a negative electrode in electrical contact with a negative electrode current collector, said current collector in electrical connection with the external circuit;
a separator positioned between and in ionic contact with a cathode and an anode;
an electrolyte in ionic contact with the positive and negative electrodes;
wherein the positive electrode comprises the positive electrode material of claim 1 ;
wherein the positive electrode further comprises fluorine as a dopant material; and
wherein the positive electrode material is cap able of providing an energy density of at least 340 mWh/g and a specific capacity of at least 110 mAh/g at 20C discharge rate during operation in a battery cell.
26. The lithium secondary cell as claimed in claim 25 , wherein D is one or more dopants wherein each dopant is selected from the group consisting of cobalt (Co), vanadium (V), and niobium (Nb).
27. The lithium secondary cell as claimed in claim 25 , wherein D is one or more dopants wherein each dopant is selected from the group consisting of cobalt (Co) and vanadium (V).