Hardened martensitic steel, method for producing a component from this steel and component obtained in this manner
View Patent ↗The invention relates to steel which is characterized by the following composition as expressed in percentages by weight: —C=0.18 0.30%, —Co=5-7%, —Cr=2-5%, —Al=1-2%, —Mo+W/2=1-4%, —V=trace 0.3%, —Nb=trace 0.1%, —B=trace−50 ppm, —Ni=10.5-15% with Ni≧7+3.5 Al, —Si=trace 0.4%, —Mn=trace 0.4%, —Ca=trace−500 ppm, —Rare earths=trace−500 ppm, —Ti=trace−500 ppm, —O=trace−200 ppm if the steel is obtained by means of powder metallurgy or trace−50 ppm if the steel is produced in air or under a vacuum from molten metal, —N=trace−100 ppm, —S=trace−50 ppm, —Cu=trace−1%, and —P=trace−200 ppm, the remainder including iron and the inevitable impurities resulting from production. The invention also relates to a method of producing a part from said steel and to the part thus obtained.
1. Method for producing a component from steel, characterized in that the method comprises the following steps prior to the finishing of the component which provides the component with its definitive shape:
preparing a steel characterized in that the composition thereof is, in percentages by weight:
C=0.18-0.30%
Co=5-7%
Cr=2-5%
Al=1-2%
Mo+W/2=1-4%
V=trace levels−0.3%
Nb=trace levels−0.1%
B=trace levels−50 ppm
Ni=10.5-15% with Ni≧7+3.5 Al
Si=trace levels−0.4%
Mn=trace levels−0.4%
Ca=trace levels−500 ppm
Rare earth elements=trace levels−500 ppm
Ti=trace levels−500 ppm
O=trace levels−200 ppm if the steel is obtained by means of powder metallurgy, or trace levels−50 ppm if the steel is obtained by means of production in air or under vacuum from liquid metal
N=trace levels−100 ppm
S=trace levels−50 ppm
Cu=trace levels−1%
P=trace levels−200 ppm
the remainder being iron and inevitable impurities resulting from the production operation;
forging the steel;
a softening tempering operation at 600-675° C. for from 4 to 20 hours followed by cooling in air;
solution heat treating at 900-1000° C. for at least 1 hour, followed by cooling in oil or air which is sufficiently rapid to prevent the precipitation of intergranular carbides in the austenite matrix; and
hardening ageing at 475-600° C. for from 5-20 h;
thereby providing steel which has an Rm at ambient temperature between 2200 and 2350 MPa.
2. Method for producing a component from steel according to claim 1 , characterized in that it further comprises a cryogenic processing operation at −50° C. or lower in order to convert all the austenite into martensite, the temperature being 200° C. or more lower than Ms, at least one of the processing operations lasting at least 2 hours, wherein the cryogenic processing operation is carried out between the cooling in oil or air and the hardening ageing.
3. Method for producing a component from steel according to claim 2 , characterized in that it further comprises a cryogenic processing operation at −80° C. or lower.
4. Method for producing a component from steel according to claim 1 , characterized in that it further comprises a processing operation for softening the martensite so obtained carried out at 150° C.-250° C. for from 4-16 hours, followed by cooling in still air.
5. Method for producing a component from steel according to claim 1 , characterized in that the component is also subject to a case-hardening or nitriding operation.
6. Method for producing a component from steel according to claim 1 , wherein the hardening ageing is from 490-525° C. for from 5-20 h.
7. Method for producing a component from steel according to claim 1 , wherein the steel which is provided-has an Rm of about 1800 MPa at 400° C.
8. Method for producing a component from steel according to claim 7 , wherein the steel which is provided has an Rp0.2 of from 1959 to 2135 MPa.
9. Method for producing a component from steel according to claim 8 , wherein C=0.20-0.25%.
10. Method for producing a component from steel according to claim 7 , wherein C=0.20-0.25%.
11. Method for producing a component from steel according to claim 1 , wherein the steel which is provided has an Rp0.2 of from 1959 to 2135 MPa.
12. Method for producing a component from steel according to claim 11 , wherein C=0.20-0.25%.
13. Method for producing a component from steel according to claim 1 , wherein C=0.20-0.25%.