Alumina ceramic for spark plug insulator

1. A ceramic material for an insulator of a spark plug comprising, in weight percent (wt %) of said ceramic material,

aluminum oxide (Al 2 O 3 ) in an amount of 98.00 wt % to 99.50 wt %;

at least one oxide of a Group 2 alkaline earth metal (Group 2 oxide) in an amount of 0.16 wt % to 0.70 wt %; said at least one Group 2 oxide including at least one of calcium oxide (CaO), magnesium oxide (MgO), beryllium oxide (BeO), strontium oxide (SrO), barium oxide (BaO), and radium oxide (RaO);

silicon dioxide (SiO 2 ) in an amount of 0.25 wt % to 0.75 wt %;

at least one oxide of a Group 4 transitional metal (Group 4 oxide) in an amount of 0.01 wt % to 0.16 wt %, said at least one Group 4 oxide including at least one of zirconium oxide (ZrO 2 ), titanium dioxide (TiO 2 ), hafnium oxide (HfO 2 ), and rutherfordium oxide (RfO 2 ); and

at least one oxide of a Group 1 alkali metal (Group 1 oxide) in an amount less than 0.0060 wt %; said at least one Group 1 oxide including at least one of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 ), rubidium oxide (Rb 2 O), cesium oxide (Cs 2 O), and francium oxide (Fr 2 O).

2. A ceramic material as set forth in claim 1 wherein said Al 2 O 3 is formed of particles having a D50 median particle size by volume of 1.2 μm to 1.8 μm.

3. A ceramic material as set forth in claim 1 wherein said Al 2 O 3 is formed of particles having a D90 particle size by volume of 2.5 μm to 6.0 μm.

4. A ceramic material as set forth in claim 1 wherein said Al 2 O 3 is formed of particles having a specific surface area of 2.0 m 2 /g to 5.0 m 2 /g.

5. A ceramic material as set forth in claim 1 including MgO in an amount of 0.01 wt % to 0.15 wt %.

6. A ceramic material as set forth in claim 1 including CaO in an amount of 0.15 wt % to 0.55 wt %.

7. A ceramic material as set forth in claim 1 including ZrO 2 and TiO 2 in an amount of 0.07 wt % to 0.10 wt %.

8. A ceramic material as set forth in claim 1 including ZrO 2 in an amount of 0.01 wt % to 0.15 wt %.

9. A ceramic material as set forth in claim 1 including TiO 2 in an amount of up to 0.01 wt %.

10. A ceramic material as set forth in claim 1 including K 2 O and Na 2 O in an amount less than 0.0060 wt %.

11. A ceramic material as set forth in claim 1 including a glass phase in an amount of 0.50 wt % to 2.0 wt %.

12. A ceramic material as set forth in claim 11 wherein said glass phase includes at least a portion of said Al 2 O 3 , said Group 2 oxides, and said SiO 2 .

13. A ceramic material as set forth in claim 12 wherein said glass phase includes, in weight percent of said glass phase, said Al 2 O 3 in an amount of 5.0 wt % to 50.0 wt %, said SiO 2 in an amount of 27.0 wt % to 50.0 wt %, and wherein said Group 2 oxides include CaO in an amount 15.0 wt % to 24.0 wt % and MgO in an amount of 0.5 wt % to 7.7 wt %.

14. A ceramic material as set forth in claim 1 including secondary crystals comprising at least a portion of said Al 2 O 3 , said Group 2 oxides, and said SiO 2 .

15. A ceramic material as set forth in claim 14 wherein said secondary crystals include at least one of calcium hexa-aluminate (CaAl 12 O 19 ) spinel (MgAl 2 O 4 ), anorthite (CaAl 2 Si 2 O 8 ), and mullite (Al 6 Si 2 O 13 ).

16. A ceramic material as set forth in claim 1 including said Al 2 O 3 in an amount of 98.85 wt %, said Group 2 oxides in an amount of 0.46 wt %, and said SiO 2 in an amount of 0.60 wt %.

17. A ceramic material as set forth in claim 1 wherein said Group 2 oxides include CaO and MgO and including said Al 2 O 3 in an amount of 98.85 wt %, said CaO in an amount of 0.39 wt %, said MgO in an amount of 0.073 wt %, said SiO 2 in an amount of 0.60 wt %, TiO 2 in an amount of 0.004 wt %, ZrO 2 in an amount of 0.08 wt %, K 2 O in an amount of 0.003 wt %, Na 2 O in an amount of 0.0007 wt %, and P 2 O 5 in an amount of 0.0027 wt %.

18. A ceramic material as set forth in claim 1 wherein said Group 2 oxides include CaO and MgO and including said Al 2 O 3 in an amount of 98.80 wt %, said CaO in an amount of 0.46 wt %, said MgO in an amount of 0.037 wt %, said SiO 2 in an amount of 0.62 wt %, TiO 2 in an amount of 0.005 wt %, ZrO 2 in an amount of 0.08 wt %, K 2 O in an amount of 0.004 wt %, Na 2 O in an amount of 0.0008 wt %, and P 2 O 5 in an amount of 0.0031 wt %.

19. A insulator formed of a ceramic material for a spark plug comprising, in weight percent (wt %) of said ceramic material, aluminum oxide (Al 2 O 3 ) in an amount of 98.00 wt % to 99.50 wt %; at least one oxide of a Group 2 alkaline earth metal (Group 2 oxide) in an amount of 0.16 wt % to 0.70 wt %; said at least one Group 2 oxide including at least one of calcium oxide (CaO), magnesium oxide (MgO), berryllium oxide (BeO), strontium oxide (SrO), barium oxide (BaO), and radium oxide (RaO);

silicon dioxide (SiO 2 ) in an amount of 0.25 wt % to 0.75 wt %;

at least one oxide of a Group 4 transition metal (Group 4 oxide) in an amount of 0.01wt % to 0.16 wt %, said at least one Group 4 oxide including at least one of zirconium oxide (ZrO 2 ), titanium dioxide (TiO 2 ), hafnium oxide (HfO 2 ), and rutherfordium oxide (RfO 2 ); and

at least one oxide of a Group 1 alkali metal (Group 1 oxide) in an amount less than 0.0060 wt %; said at least one Group 1 oxide including at least one of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O), rubidium oxide (Rb 2 O), cesium oxide (Cs 2 O), and francium oxide (Fr 2 O).

20. A spark plug including an insulator formed of a ceramic material comprising, in weight percent (wt %) of said ceramic material, aluminum oxide (Al 2 O 3 ) in an amount of 98.00 wt % to 99.50 wt %; at least one oxide of a Group 2 alkaline earth metal (Group 2 oxide) in an amount of 0.16 wt % to 0.70 wt %; said at least one Group 2 oxide including at least one of calcium oxide (CaO), magnesium oxide (MgO), beryllium oxide (BeO), strontium oxide (SrO), barium oxide (BaO), and radium oxide (RaO);

silicon dioxide (SiO 2 ) in an amount of 0.25 wt % to 0.75 wt %;

at least one oxide of a Group 4 transition metal (Group 4 oxide) in an amount of 0.01wt % to 0.16 wt %, said at least one Group 4 oxide including at least one of zirconium oxide (ZrO 2 ), titanium dioxide (TiO 2 ), hafnium oxide (HfO 2 ), and rutherfordium oxide (RfO 2 ); and

at least one oxide of a Group 1 alkali metal (Group 1 oxide) in an amount less than 0.0060 wt %; said at least one Group 1 oxide including at least one of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O), rubidium oxide (Rb 2 O), cesium oxide (Cs 2 O), and francium oxide (Fr 2 O).

21. A method of fabricating a ceramic material for an insulator of a spark plug comprising the steps of:

providing ceramic particles including, in weight percent wt % of the ceramic material, aluminum oxide (Al 2 O 3 ) having a median particle size of 1.2 μm to 1.8 μm in an amount of 98.00 wt % to 99.50 wt %, at least one oxide of a Group 2 alkali earth metal (Group 2 oxide) in an amount of 0.16 wt % to 0.60 wt %, the at least one Group 2 oxide including at least one of calcium oxide (CaO), magnesium oxide (MgO), beryllium oxide (BeO), strontium oxide (SrO), barium oxide (BaO), and radium oxide (RaO), silicon dioxide (SiO 2 ) in an amount of 0.25 wt % to 0.75 wt %, at least one oxide of a Group 4 transition metal (Group 4 oxide) in an amount of 0.01 wt % to 0.16 wt %, the at least one Group 4 oxide including at least one of zirconium oxide (ZrO 2 ), titanium dioxide (TiO 2 ), hafnium oxide (HfO 2 ), and rutherfordium oxide (RfO 2 ), at least one oxide of a Group 1 alkali metal (Group 1 oxide) in an amount less than 0.0060 wt %, and the at least one Group 1 oxide including at least one of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 3 O), rubidium oxide (Rb 2 ), cesium oxide (Cs 2 O), and francium oxide (Fr 2 O);

pressing the ceramic particles; and

sintering the ceramic particles.

22. A method of fabricating an insulator formed of a ceramic material for a spark plug comprising the steps of:

providing ceramic particles including, in weight percent wt % of the ceramic material, aluminum oxide (Al 2 O 3 ) having a median particle size of 1.2 μm to 1.8 μm in an amount of 98.00 wt % to 99.50 wt %, at least one oxide of a Group 2 alkali earth metal (Group 2 oxide) in an amount of 0.16 wt % to 0.60 wt %, the at least one Group 2 oxide including at least one of calcium oxide (CaO), magnesium oxide (MgO), beryllium oxide (BeO), strontium oxide (SrO), barium oxide (BaO), and radium oxide (RaO), silicon dioxide (SiO 2 ) in an amount of 0.25 wt % to 0.75 wt %, at least one oxide of a Group 4 transition metal (Group 4 oxide) in an amount of 0.01 wt % to 0.16 wt %, the at least one Group 4 oxide including at least one of zirconium oxide (ZrO 2 ), titanium dioxide (TiO 2 ), hafnium oxide (HfO 2 ), and rutherfordium oxide (RfO 2 ), at least one oxide of a Group 1 alkali metal (Group 1 oxide) in an amount less than 0.0060 wt % and the at least one Group 1 oxide including at least one of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O), rubidium oxide (Rb 2 O), cesium oxide (Cs 2 O), and francium oxide (Fr 2 O);

pressing the ceramic particles;

sintering the ceramic particles; and

forming the ceramic particles to a predetermined shape.