View Patent ↗A thermosetting solution composition composed of a biphenyltetracarboxylic acid compound containing a partial lower aliphatic alkyl ester of 2,3,3′,4′-biphenyltetracarboxylic acid and/or a partial lower aliphatic alkyl ester of 2,2′,3,3′-biphenyltetracarboxylic acid, an aromatic diamine compound in a molar amount larger than a molar amount of the biphenyltetracarboxylic acid compound, a partial lower aliphatic alkyl ester of 4-(2-phenylethynyl)phthalic acid compound in a molar amount as much as 1.8-2.2 times a molar amount corresponding to a difference between the molar amount of the aromatic diamine compound and the molar amount of the biphenyltetracarboxylic acid compound, and an organic solvent composed of a lower aliphatic alcohol is of value for manufacture of a prepreg.
1. A thermosetting solution composition comprising a biphenyltetracarboxylic acid compound containing at least 15 mol % of a partial lower aliphatic alkyl ester of 2,3,3′,4′-biphenyltetracarboxylic acid and/or a partial lower aliphatic alkyl ester of 2,2′,3,3′-biphenyltetracarboxylic acid, an aromatic diamine compound in a molar amount larger than a molar amount of the biphenyltetracarboxylic acid compound, said aromatic diamine compound being selected from the group consisting of p-phenylenediamine, m-phenylenediamine, 1,3-bis(4-aminophenoxy)benzene and a mixture thereof, and a partial lower aliphatic alkyl ester of 4-(2-phenylethynyl)phthalic acid compound in a molar amount as much as 1.8-2.2 times a molar amount corresponding to a difference between the molar amount of the aromatic diamine compound and the molar amount of the biphenyltetracarboxylic acid compound dissolved in an organic solvent consisting of methanol, ethanol, or a mixture of methanol and ethanol.
2. The thermosetting solution composition of claim 1 , in which each of the partial lower aliphatic alkyl ester of 2,3,3′,4′-biphenyltetracarboxylic acid, partial lower aliphatic alkyl ester of 2,2′,3,3′-biphenyltetracarboxylic acid, and partial lower aliphatic alkyl ester of 4-(2-phenylethynyl)phthalic acid compound is methyl ester or ethyl ester.
3. The thermosetting solution composition of claim 1 , in which the aromatic diamine compound comprises p-phenylenediamine, 1,3-bis(4-minophenoxy)benzene, or a mixture thereof.
4. The thermosetting solution composition of claim 1 , in which the aromatic diamine compound comprises a mixture of p-phenylenediamine and 1,3-bis(4-aminophenoxy)benzene wherein p-phenylenediamine is present in an amount of 50 to 70 molar %.
5. A process for preparing a prepreg which comprises the steps of:
impregnating a sheet matrix of a reinforcing fiber with a thermosetting solution composition of claim 1 ; and heating the impregnated sheet matrix to remove a portion of the solvent, whereby obtaining a prepreg having a volatile content in the range of 10 to 25 wt. %.
6. A thermosetting solution composition comprising a biphenyltetracarboxylic acid compound containing at least 15 mol % of a partial methyl ester of 2,3,3′,4′-biphenyltetracarboxylic acid and/or a partial methyl ester of 2,2′,3,3′-biphenyl-tetracarboxylic acid, an aromatic diamine compound in a molar amount larger than a molar amount of the biphenyltetracarboxylic acid compound, said aromatic diamine compound being selected from the group consisting of p-phenylenediamine, m-phenylenediamine, 1,3-bis(4-aminophenoxy)benzene and a mixture thereof, and a partial methyl ester of 4-(2-phenyl-ethynyl) phthalic acid compound in a molar amount as much as 1.8 - 2.2 times a molar amount corresponding to a difference between the molar amount of the aromatic diamine compound and the molar amount of the biphenyltetracarboxylic acid compound dissolved in an organic solvent consisting of ethanol.
7. The thermosetting solution composition of claim 6 , in which the aromatic diamine compound is p-phenylenediamine, 1,3-bis(4-aminophenoxy)benzene or a mixture thereof.
8. The thermosetting solution composition of claim 6 , in which the aromatic diamine compound comprises a mixture of p-phenylenediamine and 1,3-bis(4-aminophenoxy)benzene wherein p-phenylenediamine is present in an amount of 50 to 70 molar %.
9. A prepreg comprising a sheet matrix of a reinforcing fiber impregnated with a thermosetting solution composition of claim 6 .