Metal air cathode manganese oxide contained in octahedral molecular sieve
View Patent ↗An oxygen reduction electrode, e.g., an air cathode, comprising manganese oxides having octahedral molecular sieve structures as active catalyst materials and use of such an electrode as a component of a metal-air cell.
1. An electrochemical cell comprising:
an anode;
an aqueous alkaline electrolytic solution; and
an oxygen reduction electrode comprising a mixed manganese oxide catalyst comprising an octahedral molecular sieve structure and Mn 2 O 3 , wherein the octahedral molecular sieve structure and the Mn 2 O 3 are present in the mixed catalyst in a ratio between about 1:1 and about 3:1.
2. An electrochemical cell as set forth in claim 1 wherein the manganese in the mixed catalyst has an average oxidation state of less than about 3.7.
3. An electrochemical cell as set forth in claim 2 wherein the manganese in the mixed catalyst has an average oxidation state between about 3.1 and 3.7.
4. An electrochemical cell as set forth in claim 3 wherein the manganese in the mixed catalyst has an average oxidation state of about 3.3.
5. An electrochemical cell as set forth in claim 1 wherein the mixed catalyst has been calcined at a temperature between about 450° C. and about 650° C.
6. An electrochemical cell as set forth in claim 5 wherein the mixed catalyst has been calcined at a temperature between about 500° C. and about 600° C.
7. An electrochemical cell as set forth in claim 6 wherein the mixed catalyst has been calcined at a temperature of about 550° C.
8. An electrochemical cell as set forth in claim 1 wherein the octahedral molecular sieve structure and the Mn 2 O 3 are present in the mixed catalyst in a ratio of between about 1.27:1 and about 1:1.
9. An electrochemical cell as set forth in claim 8 wherein the octahedral molecular sieve structure and the Mn 2 O 3 are present in the mixed catalyst in a ratio of about 1:1.
10. An electrochemical cell as set forth in claim 1 wherein the manganese oxide contained in the mixed catalyst comprises particles having a B.E.T. surface area between about 10 m 2 /g and about 100 m 2 /g.
11. An electrochemical cell as set forth in claim 10 wherein the manganese oxide contained in the mixed catalyst comprises particles having a B.E.T. surface area between about 15 m 2 /g and about 90 m 2 /g.
12. An electrochemical cell as set forth in claim 1 wherein the manganese oxide contained in the mixed catalyst comprises particles having a mean particle size between about 0.5 μm and about 2.0 μm.
13. An electrochemical cell as set forth in claim 12 wherein the manganese oxide contained in the mixed catalyst comprises particles having a mean particle size between about 1.5 μm and 2.0 μm.
14. An electrochemical cell comprising:
an anode;
an aqueous alkaline electrolytic solution; and
an oxygen reduction electrode comprising a mixed manganese oxide catalyst comprising an octahedral molecular sieve structure and Mn 2 O 3 , wherein the manganese in the mixed catalyst has an average oxidation state between about 3.2 and 3.6.
15. An electrochemical cell as set forth in claim 14 wherein the mixed catalyst has been calcined at a temperature between about 450° C. and about 650° C.
16. An electrochemical cell as set forth in claim 14 wherein the manganese in the mixed catalyst has an average oxidation state between about 3.25 and 3.5.
17. An electrochemical cell as set forth in claim 16 wherein the manganese in the mixed catalyst has an average oxidation state of about 3.3.