Dental restorations using nanocrystalline materials
View Patent ↗Dental articles are produced using relatively low sintering temperatures to achieve high density dental articles exhibiting strengths equal to and greater than about 700 MPa. Ceramic powders comprised of nanoparticulate crystallites are used to manufacture dental articles. The ceramic powders may include sintering agents, binders and other similar additives to aid in the processing of the ceramic powder into a dental article. The ceramic powders may be processed into dental articles using various methods including, but not limited to, injection molding, gel-casting, slip casting, or electroforming, hand, cad/camming and other various rapid prototyping methods. The ceramic powder may be formed into a suspension, pellet, feedstock material or a pre-sintered blank prior to forming into the dental article.
1. A dental article manufactured by the process comprising:
mixing ceramic powder comprising nanoparticles having a crystallite size of less than about 20 nm with a sintering aid comprising metallic particles, wherein the metallic particles have a crystallite size greater than about 100 nanometers;
forming the powder mixture into a dental article;
subjecting the article to microwave radiation to densify the article;
wherein the final ceramic material exhibits at least 30% relative transmission of visible light when measured through a thickness in the range of about 0.3 to about 0.5 mm.
2. The dental article of claim 1 further comprising mixing a binder with the ceramic powder and sintering aid.
3. The dental article of claim 1 wherein the ceramic powder comprises nearly spherical particles.
4. The dental article of claim 1 wherein the dental article is selected from the group consisting of orthodontic retainers, bridges, space maintainers, tooth replacement appliances, splints, crowns, partial crowns, dentures, posts, teeth, jackets, inlays, onlays, facings, veneers, facets, implants, cylinders, abutments and connectors.
5. The dental article of claim 1 wherein the ceramic powder comprises zirconia, alumina, titania, silica, magnesia, yttria, ceria and mixtures thereof.
6. The dental article of claim 5 wherein the zirconia is yttria-stabilized tetragonal zirconia.
7. The dental article of claim 2 wherein the binder is selected from the group consisting of polyacrylic binders, polyvinyl alcohol (PVA) binders, polyvinyl butyral (PVB) binders, waxes, and mixtures thereof.
8. The dental article of claim 7 wherein the waxes comprise natural waxes, synthetic waxes or mixtures thereof.
9. The dental article of claim 8 wherein the waxes comprises paraffin wax, polyethylene wax, carnauba wax, bee wax, stearic and oleic acids, and mixtures thereof.
10. The dental article of claim 1 wherein the metallic particles are added as oxides, salts, organometallic compounds, or precursor compounds.
11. The dental article of claim 1 wherein the metallic particles are added in the form of colloids or powders.
12. The dental article of claim 1 wherein the metallic particles are selected from the group consisting of Si, Al, Mg, Zr, Y, Ce, Ta metal and mixtures thereof.
13. The dental article of claim 1 wherein forming the powder mixture into a dental article is performed by hand, by CAD/CAM methods or by rapid prototyping methods.
14. The dental article of claim 1 wherein the dental article is polycrystalline and comprises grains greater than about one hundred nanometers.
15. The dental article of claim 1 wherein the dental article comprises grain sizes from about one hundred nanometers to about 500 nanometers.
16. The dental article of claim 1 wherein the metallic particles are microscopic in size.
17. The dental article of claim 1 wherein the metallic particles are macroscopic in size.
18. The dental article of claim 14 wherein the polycrystalline grains are comprised of clusters of nanocrystallites.
19. The dental article of claim 14 wherein the polycrystalline grains comprise nano, micro, and macro particles.