Lubricant composition for hot forming
View Patent ↗The present invention provides a lubricant composition for hot forming which makes it possible to provide lubricity at 80° C. or more without being peeled or washed by the roll cooling water, and which is easily washed under 40° C. without having water resistance. The lubricant composition for hot forming of the present invention comprises: a solid lubricant from 10 to 40% by mass; water-dispersible synthetic resin from 5 to 20% by mass; inorganic acid amine salt from 0.5 to 5% by mass; and water from 45 to 80% by mass.
1. A lubricant composition for hot forming comprising: solid lubricant from 10 to 40% by mass; water-dispersible synthetic resin from 5 to 20% by mass; inorganic acid amine salt from 0.5 to 5% by mass, the inorganic acid of said inorganic acid amine salt being selected from boric acid, molybdenum acid, or tungsten acid; and water from 45 to 80% by mass, for 100% by mass of the total mass of the lubricant composition,
wherein said water-dispersible synthetic resin is a resin obtained by polymerization with the following a first to a fourth ingredients,
a first ingredient: main monomer from 85 to 99.7% by mass,
a second ingredient: monomer having functioning group from 0.1 to 7% by mass,
a third ingredient: cross-linking monomer from 0 to 5% by mass,
a fourth ingredient: co-polymeric surfactant from 2.1 to 7% by mass, for 100% by mass of the total mass of said first to fourth ingredients,
said main monomer is two or more monomers selected from methacrylic ester or acrylic ester, and
solubility of said monomer in the water is 1% or less.
2. A lubricant composition for hot forming comprising: solid lubricant from 10 to 40% by mass; water-dispersible synthetic resin from 5 to 20% by mass; inorganic acid amine salt from 0.5 to 5% by mass, the inorganic acid of said inorganic acid amine salt being selected from boric acid; molybdenum acid, or tungsten acid; and water from 45 to 80% by mass, for 100% by mass of the total mass of the lubricant composition,
wherein said water-dispersible synthetic resin is a resin obtained by polymerization with the following a first to a fourth ingredient,
a first ingredient: main monomer from 88 to 97.4% by mass,
a second ingredient: monomer having functioning group from 0.2 to 5.5% by mass,
a third ingredient: cross-linking monomer from 0 to 3% by mass,
a fourth ingredient: co-polymeric surfactant from 2.4 to 4.8% by mass, for 100% by mass of the total mass of said first to fourth ingredients,
said main monomer is two or more monomers selected from methacrylic ester or acrylic ester, and
solubility of said monomer in the water is 1% or less.
3. A lubricant composition for hot forming according to claim 1 , wherein the functioning group of said monomer having functioning group is selected from a group consisting of carboxyl group, epoxy group, amino group, and acetoacetyl group.
4. A lubricant composition for hot forming according to claim 1 , wherein said co-polymeric surfactant is an anionic system co-polymeric surfactant.
5. A lubricant composition for hot forming according to claim 1 , wherein ingredient of monomer, constituting said water-dispersible synthetic resin further comprising a fifth ingredient: polymeric monomer having alkoxysilyl group from 0.01 to 2% by mass.
6. A lubricant composition for hot forming according to claim 2 , wherein ingredient of monomer, constituting said water-dispersible synthetic resin further comprising a fifth ingredient: polymeric monomer having alkoxysilyl group from 0.01 to 2% by mass.
7. A lubricant composition for hot forming according to claim 1 , wherein the amine salt of said inorganic acid is a boric amine salt.
8. A lubricant composition for hot forming according to claim 2 , wherein the amine salt of said inorganic acid is a boric amine salt.
9. A lubricant composition for hot forming according to claim 1 , in a water resistance test, peeling below 15% is shown at the temperature of 80° C., and in water washability test, peeling of 85% or more is shown at the temperature of 40° C.
10. A lubricant composition for hot forming according to claim 2 , in a water resistance test, peeling below 15% is shown at the temperature of 80° C., and in water washability test, peeling of 85% or more is shown at the temperature of 40° C.
11. A method for producing seamless pipe or tube comprising the steps of:
applying of the lubricant composition for hot forming as claimed in claim 1 to a mandrel bar, and
continuously rolling a pipe or tube by utilizing this mandrel bar.
12. A method for producing seamless pipe or tube comprising the steps of:
applying of the lubricant composition for hot forming as claimed in claim 2 to a mandrel bar, and
continuously rolling a pipe or tube by utilizing this mandrel bar.