Colorant concentrates for thermoplastic biofiber composites
View Patent ↗Color concentrates for thermoplastic biofiber composites are disclosed. The concentrates employ three factors to achieve concentrated delivery of color to the processing machine and excellent and substantially uniform dispersion of color in the processing machine: melt flow of the concentrate exceeding at least 4 g/10 min. using ASTM D-1238; pellet size of the concentrate such that at least 50 pellets weigh less than one gram; and weight percent of the colorant ingredients in the concentrate exceeding at least 30 weight percent.
1. A method of using a colorant concentrate for a thermoplastic biofiber composite, comprising the steps of:
(a) melt mixing the concentrate, biofiber, and a thermoplastic to form a melt composite; and
(b) shaping the melt composite into a thermoplastic biofiber composite having coloration,
wherein the concentrate comprises pellets of a shape of microbeads formed from extrusion through a mini-bead die and comprising carrier resin and colorant,
wherein the carrier resin comprises low-density polyethylene, linear-low-density polyethylene, or polypropylene and
wherein
(1) melt flow index of the concentrate exceeds at least 4 g/10 min. using ASTM D-1238;
(2) size of the pellets results in at least 50 pellets having a total mass of less than one gram; and
(3) weight percent of the colorant exceeds at least 30 weight percent of the weight of the concentrate.
2. The method of claim 1 , wherein the concentrate is made by the steps of:
(i) melt mixing the carrier resin, the colorant, and any optional additives in a chamber to form a melt concentrate;
(ii) extruding the melt concentrate through the mini-bead die; and
(iii) pelletizing the melt concentrate under water to form pellets of the shape of the microbeads.
3. The method of claim 1 , wherein the colorant comprises a pigment, a dye, a combination of pigments, a combination of dyes, a combination of pigments and dye, a combination of pigment and dyes, or a combination of pigments and dyes.
4. The method of claim 1 , wherein the concentrate has a minimum melt flow index of least 6 g/10 min.
5. The method of claim 1 , wherein the colorant has a particle size ranging from about 0.01 to about 10,000 micrometers.
6. The method of claim 1 , wherein the concentrate further comprises additives providing special features selected from the group consisting of granites, translucents, pearlescents, metallics, fluorescents, iridescents, marbles, and combinations thereof.
7. The method of claim 1 , wherein the concentrate further comprises functional additives selected from the group consisting of anti-oxidants, anti-stats, acetaldehyde scavengers, blowing agents, waxes, ultraviolet light stabilizers, lubricants, surfactants, biocides, anti-microbials, exfoliated nanoclays, and combinations thereof.
8. The method of claim 1 , wherein the amount of carrier resin ranges from about 20 to about 65 weight percent of concentrate and wherein the amount of colorant ranges from about 30 to about 75 weight percent of the concentrate.
9. The method of claim 1 , wherein the ratio of concentrate to resin ranges from about 1:99 to 4:96.
10. The method of claim 9 , wherein the biofiber is selected from the group consisting of wood fibers, wood flour, bamboo fibers, rice hulls, sugar cane fiber, ground newsprint, ground magazines, ground books, ground cardboard, wood pulps, wheat chaff, oat chaff, barley chaff, oat, coconut shells, peanut shells, walnut shells, straw, corn husks, corn stalks, jute, hemp, bagasse, bamboo, flax, kenaf, and combinations thereof.
11. The method of claim 9 , wherein the thermoplastic resin matrix is selected from the group consisting of polyolefins and polyvinyl chloride.
12. The method of claim 6 , wherein the ratio of concentrate to resin ranges from about 1:99 to 4:96.
13. The method of claim 12 , wherein the biofiber is selected from the group consisting of wood fibers, wood flour, bamboo fibers, rice hulls, sugar cane fiber, ground newsprint, ground magazines, ground books, ground cardboard, wood pulps, wheat chaff, oat chaff, barley chaff, oat, coconut shells, peanut shells, walnut shells, straw, corn husks, corn stalks, jute, hemp, bagasse, bamboo, flax, kenaf, and combinations thereof.
14. The method of claim 12 , wherein the thermoplastic resin matrix is selected from the group consisting of polyolefins and polyvinyl chloride.
15. The method of claim 7 , wherein the ratio of concentrate to resin ranges from about 1:99 to 4:96.
16. The method of claim 15 , wherein the biofiber is selected from the group consisting of wood fibers, wood flour, bamboo fibers, rice hulls, sugar cane fiber, ground newsprint, ground magazines, ground books, ground cardboard, wood pulps, wheat chaff, oat chaff, barley chaff, oat, coconut shells, peanut shells, walnut shells, straw, corn husks, corn stalks, jute, hemp, bagasse, bamboo, flax, kenaf, and combinations thereof.
17. The method of claim 15 , wherein the thermoplastic resin matrix is selected from the group consisting of polyolefins and polyvinyl chloride.