View Patent ↗Processes for manufacturing a thin film composite membrane comprising multi-walled carbon nanotubes include contacting under interfacial polymerization conditions an organic solution comprising a polyacid halide with an aqueous solution comprising a polyamine to form a thin film composite membrane on a surface of a porous base membrane; at least one of the organic solution and the aqueous solution further including multi-walled carbon nanotubes having an outside diameter of less than about 30 nm.
1. A process for manufacturing a thin film composite membrane comprising multi-walled carbon nanotubes, said process comprising contacting under interfacial polymerization conditions an organic solution comprising a polyacid halide with an aqueous solution comprising a polyamine to form a thin film composite membrane on a surface of a porous base membrane;
and contacting the thin film composite membrane with a sodium hypochlorite solution, to yield a thin film composite membrane having salt passage of less than 0.4% and flux of at least 7.5×10 −5 cm 3 /s-cm 2 -atm;
wherein at least one of the organic solution and the aqueous solution further comprises multi-walled carbon nanotubes having an outside diameter of less than 8 nm.
2. A process according to claim 1 , wherein the organic solution comprises of the multi-walled carbon nanotubes, and the aqueous solution is free of the multi-walled carbon nanotubes.
3. A process according to claim 1 , wherein the concentration of the multi-walled carbon nanotubes is at least 0.025% w/w.
4. A process according to claim 1 , wherein the concentration of the multi-walled carbon nanotubes ranges from about 0.025% w/w to about 10% w/w.
5. A process according to claim 1 , wherein the concentration of the multi-walled carbon nanotubes ranges from about 0.025% w/w to about 5% w/w.
6. A process according to claim 1 , wherein the concentration of the multi-walled carbon nanotubes ranges from about 0.05% w/w to about 1% w/w.
7. A process according to claim 1 , wherein the inside diameter of the multi-walled carbon nanotubes is less than about 8 nm.
8. A process according to claim 1 , wherein the inside diameter of the multi-walled carbon nanotubes is about 2-5 nm.
9. A process according to claim 1 , wherein the polyacid halide is trimesoyl chloride.
10. A process according to claim 1 , wherein the polyamine is para-phenylene diamine.
11. A process according to claim 1 , wherein the concentration of sodium hypochlorite in the solution ranges from about 50 ppm to about 4000 ppm.
12. A thin film composite membrane prepared by the process of claim 1 .
13. A reverse osmosis element comprising a thin film composite membrane according to claim 1 .
14. A desalination system comprising at least one reverse osmosis element according to claim 13 .
15. A desalination process comprising contacting seawater or brackish water with a thin film composite membrane according to claim 13 .