Accelerated cure of isocyanate terminated prepolymers
View Patent ↗A prepolymer mixture for preparing a polyurethane elastomer, the mixture comprising an isocyanate terminated prepolymer and a nitrogen-containing organic salt. The nitrogen-containing organic salt may be selected from the group consisting of an ammonium salt, an imidazolium salt, a pyridinium salt, a pyrrolidinium salt, a piperidinium salt, and a morpholinium salt.
1. A prepolymer mixture for preparing a polyurethane elastomer, comprising:
(a) an isocyanate terminated prepolymer which is the reaction product of a diisocyanate and a polyol;
(b) from 0.5 to 5 parts per hundred, based on the entire weight of the prepolymer mixture, of an imidazolium chloride or sulfate salt; and
(c) a methylenedianiline metal salt coordination complex chain extender.
2. The prepolymer mixture of claim 1 , wherein the nitrogen-containing organic salt is present in an amount of at least 1 part per hundred based on the weight of the isocyanate terminated prepolymer.
3. The prepolymer mixture of claim 1 , wherein the prepolymer mixture comprises less than 0.5 weight percent residual isocyanate monomer.
4. The prepolymer mixture of claim 1 , wherein the diisocyanate is selected from the group consisting of toluene diisocyanate, diphenylmethane diisocyanate, para-phenylene diisocyanate, naphthalene diisocyanate, DPDI, 1,6-hexane diisocyanate, isophorone diisocyanate, methylene bis (p-cyclohexyl isocyanate), 3,3′-bitoluene diisocyanate, diphenyl 4,4′-diisocyanate, tetramethylxylylene diisocyanate, and polymeric MDI.
5. The prepolymer mixture of claim 1 , wherein the polyol is a polyether polyol selected from the group consisting of poly(tetramethylene ether) glycol, polypropylene glycol, and polyethylene glycol.
6. The prepolymer mixture of claim 1 , wherein the polyol is a polyester polyol reaction product of adipic acid, succinic acid, or isophthalic acid with one or more glycols.
7. The prepolymer mixture of claim 1 , wherein the isocyanate terminated prepolymer has a Brookfield viscosity, measured at 25° C., ranging from 10 centipoise to 100,000 centipoise.
8. A polyurethane elastomer comprising the reaction product of an isocyanate terminated prepolymer and a methylenedianiline metal salt coordination complex chain extender in the presence of an imidazolium chloride or sulfate salt, wherein the nitrogen-containing organic salt is present in the polyurethane elastomer in an amount ranging from 1 to 10 parts per hundred based on the total weight of the elastomer.