Rigid foamed synthetic resin and process for its production
View Patent ↗Provided is a process for producing a rigid foamed synthetic resin, wherein, as a blowing agent, a hydrocarbon compound and water are used, and a rigid foamed synthetic resin provided with dimensional stability, heat insulating properties, and possibly reduced weight can be obtained. The process involves reacting a polyol (P) with a polyisocyanate (I) in the presence of a blowing agent, a foam stabilizer and a catalyst, wherein the blowing agent has at least a C 2-8 hydrocarbon compound and water; the polyol (P) has a specific polyesterpolyol (A), a specific polyetherpolyol (B), and a polymer-dispersed polyol (Z) having fine polymer particles (M) dispersed; and the isocyanate index of the polyol (P) and the polyisocyanate (I) is over 200 and at most 400.
1. A process for producing a rigid foamed synthetic resin, the process comprising:
reacting a polyol (P) with a polyisocyanate (I) in the presence of a blowing agent, a foam stabilizer, and a catalyst,
wherein the blowing agent comprises a C 2-8 hydrocarbon compound and water,
wherein the polyol (P) comprises a polyesterpolyol (A) having a hydroxyl value of from 100 to 400 mgKOH/g, obtained by polycondensation of a monomer comprising an aromatic compound, a polyetherpolyol (B) having an average hydroxyl value of from 100 to 500 mgKOH/g, and a polymer-dispersed polyol (Z) having fine polymer particles (M) dispersed in a base polyol (W);
wherein a content of the polyesterpolyol (A) in the polyol (P), based on 100 mass % of the polyol (P), is from 50 to 95 mass %,
wherein a total content of the polyetherpolyol (B) and the polymer-dispersed polyol (Z) in the polyol (P), based on 100 mass % of the polyol (P), is from 5 to 50 mass %,
wherein a mass proportion of the fine polymer particles (M) to a total mass (100 mass %) of the polyetherpolyol (B) and the polymer-dispersed polyol (Z) is from 0.02 to 10 mass %,
wherein a isocyanate index of the polyol (P) and the polyisocyanate (I) is over 200 and at most 400; and
wherein the polyol (P) has an average hydroxyl value of from 100 to 450 mgKOH/g.
2. The process of claim 1 , wherein the polyetherpolyol (B) comprises at least one of a
Polyol (B1), a polyoxyalkylenepolyol having an average hydroxyl value of from 100 to 700 mgKOH/g, obtained by ring-opening addition polymerization of an alkylene oxide with an initiator comprising an aromatic compound,
and
Polyol (B2), a polyoxyalkylenepolyol having an average hydroxyl value of from 100 to 800 mgKOH/g, obtained by ring-opening addition polymerization of an alkylene oxide with an initiator comprising at least one of an aliphatic amine and an alicyclic amine.
3. The process of claim 2 , wherein the polyetherpolyol (B) comprises at least one polyol (B1) wherein the initiator for (B1) is selected from the group consisting of a Mannich condensate, diaminotoluene, and bisphenol A.
4. The process of claim 2 , wherein the polyetherpolyol (B) comprises the polyol (B2), and
wherein the initiator for (B2) comprises a piperazine.
5. The process of claim 1 , wherein the C 2-8 hydrocarbon compound of the blowing agent comprises at least one selected from the group consisting of propane, butane, n-pentane, isopentane, cyclopentane, hexane, and cyclohexane.
6. The process of claim 1 , wherein the C 2-8 hydrocarbon compound of the blowing agent is present in an amount of from 5 to 50 parts by mass per 100 parts by mass of the polyol (P).
7. The process of claim 1 , wherein a mass proportion of the fine polymer particles (M) in the polyol (P), based on 100 mass % of the polyol (P), is from 0.001 to 5 mass %.
8. The process of claim 1 , wherein the base polyol (W) comprises at least 5 mass %
Polyetherpolyol (W1), a polyetherpolyol having an average hydroxyl value of at most 84 mgKOH/g and an oxyethylene group content of at least 40 mass % in the entire polyetherpolyol (W1).
9. The process of claim 1 , wherein the base polyol (W) has an average hydroxyl value of from 200 to 800 mgKOH/g, and
wherein the fine polymer particles (M) are fine polymer particles obtained by polymerization of a monomer comprising acrylonitrile.
10. The process of claim 2 , wherein the polyol (B2) is present and the initiator for polyol (B2) comprises an alicyclic amine.
11. The process of claim 2 , wherein the polyol (B2) is present and the initiator for polyol (B2) comprises an aliphatic amine.
12. The process of claim 2 , wherein the polyol (B2) is present and the initiator for (B2) comprises an aliphatic amine and an alicyclic amine.
13. The process of claim 2 , wherein the polyol (B1) is present and the initiator for (B1) comprises a Mannich condensate.
14. The process of claim 2 , wherein the polyol (B1) is present and the initiator for (B1) comprises diaminotoluene.
15. The process of claim 2 , wherein the polyol (B1) is present and the initiator for (B1) comprises bisphenol A.
16. The process of claim 1 , wherein the blowing agent comprises butane.
17. The process of claim 1 , wherein the blowing agent comprises n-pentane.
18. The process of claim 1 , wherein the blowing agent comprises cyclopentane.
19. The process of claim 1 , wherein the blowing agent comprises isopentane.
20. The process of claim 1 , wherein the blowing agent comprises isopentane and cyclopentane.