Organic/inorganic composite porous membrane and electrochemical device using the same
View Patent ↗The present invention provides an organic/inorganic composite porous separator, which comprises: (a) a porous substrate having pores; and (b) an organic/inorganic composite layer formed by coating at least one region selected from the group consisting of a surface of the substrate and a part of pores present in the substrate with a mixture of inorganic porous particles and a binder polymer, wherein the inorganic porous particles have a plurality of macropores with a diameter of 50 nm or greater in the particle itself thereby form a pore structure, a manufacturing method thereof, and an electrochemical device using the same. As an additional pathway for lithium ions is created due to a number of pores existing in the inorganic porous particle itself, degradation in the battery performance can be minimized, and energy density per unit weight can be increased by the weight loss effect.
1. A manufacturing method of the organic/inorganic composite porous separator comprising the steps of:
(a) dispersing inorganic precursors and heat-decomposable compounds in a dispersion medium, misting the inorganic precursor solution, and performing a thermal decomposition and a crystallization process, to thereby prepare inorganic porous particles, wherein the inorganic porous particles have a plurality of macropores, said macropores having a diameter of 50 nm or greater in the particle itself thereby forming a pore structure;
(b) adding and mixing the inorganic porous particles obtained from step (a) with a polymer solution containing a binder polymer; and
(c) coating the mixture obtained from step (b) on at least one region selected from the group consisting of a surface of a porous substrate having pores and a part of the pores in the porous substrate, following by drying.
2. The method according to claim 1 , wherein the heat-decomposable compounds are polymer or blowing agent decomposed or pyrolyzed at a temperature lower than a melting point of the inorganic material.
3. The method according to claim 1 , wherein temperature for the thermal decomposition in the step (a) is higher than a decomposition temperature of the heat-decomposable compounds.