Silica particles and method for producing the same
View Patent ↗The present invention provides silica particles including primary particles, the primary particles having an average particle diameter in a range of from about 100 nm to about 500 nm, a particle size distribution index in a range of from about 1.40 to about 1.80, and an average roundness in a range of from about 0.5 to about 0.85, and about 95% or more, by number of particles, of the primary particles satisfying following Formula (1) with respect to a roundness (R) and a particle diameter (D) (nm): R=α×D /1000+β Formula (1) (−2.5≦α≦−0.9, 0.8≦β≦1.2).
1. Silica particles for an external additive of a toner, the silica particles comprising:
the primary particles having:
an average particle diameter in a range of from about 130 nm to about 430 nm,
a particle size distribution index in a range of from about 1.52 to about 1.75, where the particle distribution index means a square root of a value obtained by dividing a 84% diameter with a 16% diameter with respect to a cumulative frequency of circle-equivalent diameters, and
an average roundness in a range of from about 0.5 to about 0.85,
wherein:
about 95% or more, by number of particles, of the primary particles satisfy the following Formula (1) with respect to a roundness (R) and a particle diameter (D) (nm):
R=α×D/ 1000+β Formula (1)
(−1.9≦α≦−0.9, 0.82≦β≦1.11),
the average roundness is a 50% cumulative frequency of a roundness of 100 primary particles as obtained by image analysis using the following Formula (2):
R= 4π×( A/I 2 ) Formula (2)
where R represents the roundness of a primary particle in an image, I represents a perimeter of the primary particle in the image, and A represents a projected area of the primary particle in the image, and
a surface of the silica particles is hydrophobized with an organosilicon compound comprising a trimethylsilyl group, the organosilicon compound being at least one selected from the group consisting of a silazane compound and a silane compound.
2. The silica particles according to claim 1 , wherein the organosilicon compound comprising a trimethylsilyl group comprises a trimethylmethoxysilane or a hexamethyldisilazane.
3. The silica particles according to claim 1 , wherein an added amount of the organosilicon compound is in a range of from about 1% by weight to about 100% by weight with respect to an amount of the silica particles.
4. The silica particles according to claim 1 , wherein an added amount of the organosilicon compound is in a range of from about 5% by weight to about 80% by weight with respect to an amount of the silica particles.
5. A method for producing the silica particles according to claim 1 , the method comprising:
providing an alkali catalyst solution, which includes a first alkali catalyst at a concentration of from about 0.6 mol/L to about 0.85 mol/L, in a solvent comprising an alcohol; and
supplying tetraalkoxysilane and a second alkali catalyst to the alkali catalyst solution;
the tetraalkoxysilane being supplied at a supply rate of from about 0.006 mol/(mol·min) to about 0.009 mol/(mol·min) with respect to 1 mol of the alcohol in the alkali catalyst solution; and
the second alkali catalyst being supplied in an amount of from about 0.1 mol to about 0.4 mol per minute with respect to 1 mol of a total supply amount of the tetraalkoxysilane supplied per minute.
6. The method for producing the silica particles according to claim 5 , wherein the solvent comprising the alcohol is an alcohol or a mixed solvent comprising the alcohol and at least one solvent selected from the group consisting of water, ketones, ethylene glycol monoethers, monoesters of ethylene glycol monoethers, and ethers.
7. The method for producing the silica particles according to claim 6 , wherein an amount of the alcohol with respect to the at least one solvent is about 80% by weight or more.
8. The method for producing the silica particles according to claim 5 , wherein the first alkali catalyst is at least one selected from the group consisting of ammonia, urea, monoamines, and a quaternary ammonium salt.
9. The method for producing the silica particles according to claim 5 , wherein the tetraalkoxysilane is at least one selected from the group consisting of tetramethoxysilane, tetraethoxysilane, tetrapropoxysilane and tetrabutoxysilane.
10. The method for producing the silica particles according to claim 5 , wherein the supply rate of the tetraalkoxysilane with respect to an amount by mol of the alcohol in the alkali catalyst solution is from about 0.0065 mol/(mol·min) to about 0.0085 mol/(mol·min).