Lithium manganese phosphate/carbon nanocomposites as cathode active materials for secondary lithium batteries
View Patent ↗The invention relates to a lithium manganese phosphate/carbon nanocomposite as cathode material for rechargeable electrochemical cells with the general formula Li x Mn y M 1-y (PO 4 ) z /C where M is at least one other metal such as Fe, Ni, Co, Cr, V, Mg, Ca, Al, B, Zn, Cu, Nb, Ti, Zr, La, Ce, Y, x=0.8-1.1, y=0.5-1.0, 0.9<z<1.1, with a carbon content of 0.5 to 20% by weight, characterized by the fact that it is obtained by milling of suitable precursors of Li x Mn y M 1-y (PO 4 ) Z with electro-conductive carbon black having a specific surface area of at least 80 m 2 /g or with graphite having a specific surface area of at least 9.5 m 2 /g or with activated carbon having a specific surface area of at least 200 m 2 /g. The invention also concerns a process for manufacturing said nanocomposite.
1. A process for the production of a lithium manganese phosphate/carbon nanocomposite as cathode material for rechargeable electrochemical cells with the general formula Li x Mn y M 1-y (PO 4 ) z /C where M is at least one other metal such as Fe, Ni, Co, Cr, V, Mg, Ca, Al, B, Zn, Cu, Nb, Ti, Zr, La, Ce, Y, x=0.8-1.1, y=0.5-1.0, 0.9≦z≦1.1, with a carbon content of 0.5 to 20% by weight, comprising milling of precursors of Li x Mn y M 1-y (PO 4 ) z with electro-conductive carbon black having a specific surface area of at least 80 m 2 /g or with graphite having a specific surface area of at least 9.5 m 2 /g or with activated carbon having a specific surface area of at least 200 m 2 /g and heating to form the lithium manganese phosphate/carbon nanocomposite.
2. A process for the production of a lithium manganese phosphate/carbon nanocomposite as cathode material for rechargeable electrochemical cells with the general formula Li x Mn y M 1-y (PO 4 ) z /C where M is at least one other metal such as Fe, Ni, Co, Cr, V, Mg, Ca, Al, B, Zn, Cu, Nb, Ti, Zr, La, Ce, Y, x=0.8-1.1, y=0.5-1.0, 0.9≦z≦1.1, with a carbon content of 0.5 to 20% by weight, comprising milling of precursors of Li x Mn y M 1-y (PO 4 ) z with electro-conductive carbon black having a specific surface area of at least 80 m 2 /g or with graphite having a specific surface area of at least 9.5 m 2 /g or with activated carbon having a specific surface area of at least 200 m 2 /g and heating to form the lithium manganese phosphate/carbon nanocomposite, wherein a metal precursor for the Li x Mn y M 1-y (PO 4 ) z is added in stoichiometric excess with respect to a phosphate precursor.
3. A process for the production of a lithium manganese phosphate/carbon nanocomposite as cathode material for rechargeable electrochemical cells with the general formula Li x Mn y M 1-y (PO 4 ) z /C where M is at least one other metal such as Fe, Ni, Co, Cr, V, Mg, Ca, Al, B, Zn, Cu, Nb, Ti, Zr, La, Ce, Y, x=0.8-1.1, y=0.5-1.0, 0.9<z<1.1, with a carbon content of 0.5 to 20% by weight, comprising milling of precursors of Li x Mn y M 1-y (PO 4 ) z with electro-conductive carbon black having a specific surface area of at least 80 m 2 /g or with graphite having a specific surface area of at least 9.5 m 2 /g or with activated carbon having a specific surface area of at least 200 m 2 /g and heating to form the lithium manganese phosphate/carbon nanocomposite, wherein a phosphate precursor for the Li x Mn y M 1-y (PO 4 ) z is added in stoichiometric excess with respect to a metal precursor of the Li x Mn y M 1-y (PO 4 ) z .
4. The process according to claim 1 in which milling is carried out under air or inert gas atmosphere.
5. The process according to claim 1 carried out in dry conditions or in the presence of a solvent.
6. The process according to claim 1 in which the product of milling is heated for crystallization to 300-600° C.
7. The process according to claim 1 in which heat treatment is carried out under a vacuum or inert gas atmosphere.
8. The process according to claim 1 in which heat treatment is carried out under a reducing gas atmosphere.
9. The process according to claim 1 wherein said metal oxide bonding layer is a manganese oxide bonding layer consisting of either Mn 3 O 4 (haussmanite), β-MnO 2 (pyrolusite), MnO (manganosite), MnOOH (groutite) or Mn1.85O.6H 2 O (birnessite).