Methods of increasing toughness of immiscible polymer blends
An immiscible polymer blend that includes an amount of poly(trimethylene terephthalate) (PTT) and an amount of poly(methylmethacrylate) (PMMA). A method for preparing an immiscible polymer blend by (a) identifying a first polymeric component and a second polymeric component as immiscible when blended; (b) combining the first polymeric component and the second polymeric component; and (c) mixing the first polymeric component and the second polymeric component to produce an immiscible polymer blend that includes structures in the blend having a maximum size of less than about 1,000 μm is also presented. An article that includes an immiscible polymer blend of poly(trimethylene terephthalate) (PTT) and poly(methylmethacrylate) (PMMA) and an article formed from an immiscible polymer blend prepared by the method of the present invention are also presented.
1. An immiscible polymer blend consisting of an amount of poly(trimethylene terephthalate) (PTT) ranging from 80 wt % to 95 wt % and an amount of poly(methylmethacrylate) (PMMA) ranging from 5 wt % to 20 wt % to total 100 wt %, wherein structures in the blend have a maximum size from about 0.9 μm to about 1,000 μm.
2. The blend of claim 1 , wherein the amount of PTT ranges from 85 wt % to 95 wt % and the amount of PMMA ranges from 5 wt % to 15 wt % to total 100 wt %.
3. An article comprising the polymer blend of claim 1 .
4. The article of claim 3 , wherein said article is selected from the group consisting of composite building materials, railroad ties, poles, marine pilings, simulated tree trunks, trash receptacles, boxes, cartons, doormats, floor coverings, lawn decorations and ornaments, automobile parts, toys, wagons and gardening carts, buildings and sheds, furniture, tables and chairs, park benches, and housings for electronic components.
5. The article of claim 3 , wherein said composite building material is selected from the group consisting of dimensional lumber, beams, tongue-and-groove decking panels, blocks, boards, and sheets.
6. A method for preparing an immiscible polymer blend comprising:
a) combining an amount of poly(trimethylene terephthalate) (PTT) ranging from 80 wt % to 95 wt % and an amount of poly(methylmethacrylate) (PMMA) ranging from 5 wt % to 20 wt % to total 100 wt %; and
mixing the PTT and PMMA with a single screw extruder with recirculating high elongational flow mixing elements to produce an immiscible polymer blend comprising structures in the blend having a maximum size from about 0.9 μm to about 1,000 μm.
7. An article formed from an immiscible polymer blend prepared by the method of claim 6 .
8. The article of claim 7 , wherein said article is selected from the group consisting of composite building materials, railroad ties, poles, marine pilings, simulated tree trunks, trash receptacles, boxes, cartons, doormats, floor coverings, lawn decorations and ornaments, automobile parts, toys, wagons and gardening carts, buildings and sheds, furniture, tables and chairs, park benches, and housings for electronic components.
9. The article of claim 8 , wherein said composite building material is selected from the group consisting of dimensional lumber, beams, tongue-and-groove decking panels, blocks, boards, and sheets.