Borate and polymer compositions for the repair and maintenance of railroad ties
A remedial railroad tie repair treatment capable of extending the useful life of a railroad tie. The remedial repair treatment comprises a mixture of a borate solution and a chemical tie plugging compound combined that, when applied to a wooden area of interest, will delay the decay thereof and facilitate penetration of the borate through the wood fibers. The remedial repair treatment may alternatively comprise sequential application of the borate solution and the plugging compound to the wooden area of interest.
1 . A composition for the treatment of railroad ties, comprising: a curable polymer composition; and a borate compound.
2 . The composition of claim 1 , wherein the polymer composition is cured by an exothermic reaction.
3 . The composition of claim 1 , wherein the polymer composition is selected from the group consisting of: a polyurethane compound, a polyurea compound, an epoxy compound, and combinations thereof.
4 . The composition of claim 1 , wherein the polymer composition is a 2-component polyurethane compound comprising an isocyanate and a polyol.
5 . The composition of claim 4 , wherein the polyurethane compound comprises a ratio of isocyanate to polyol of about 1:1.
6 . The composition of claim 4 , wherein the polyurethane compound comprises a ratio of isocyanate to polyol of about 1:2.
7 . The. composition of claim 4 , wherein the borate compound is incorporated into the polyol in an amount of about 2.5% borate by weight.
8 . The composition of claim 1 , wherein the polymer composition has a density in a range of about 38 to 45 pounds per cubic foot after curing.
9 . The composition of claim 1 , wherein the borate compound comprises a solution or suspension in a liquid medium of about 20% borate by weight.
10 . A method for the repair of damaged railroad ties, comprising:
applying a borate compound to the damaged surface of the railroad tie;
applying a curable polymer composition to the damaged surface of the railroad tie; and
curing the polymer composition to repair the damaged surface of the railroad tie.
11 . The method of claim 10 , wherein the polymer composition is cured by an exothermic reaction.
12 . The method of claim 10 , wherein the borate compound comprises a solution or suspension in a liquid medium of about 20% borate by weight.
13 . The method of claim 10 , further comprising the steps of:
mixing the borate compound and polymer composition; and
applying the mixture to the damaged surface of the railroad tie.
14 . The method of claim 13 , wherein the polymer composition is a 2-component polyurethane compound comprising an isocyanate and a polyol.
15 . The method of claim 14 , further comprising the steps of:
incorporating the borate compound into the isocyanate and/or polyol; and
applying the mixture of the borate compound and polymer composition to the damaged surface of the railroad tie.
16 . The method of claim 15 , wherein the borate compound is blended into the polyol in an amount of about 2.5% borate by weight.
17 . The method of claim 10 , wherein the borate compound comprises a solution or suspension in a liquid medium, and further comprising the step of applying the borate compound to the damaged surface of the railroad tie by spraying.
18 . The method of claim 10 , wherein the borate compound comprises a solution or suspension in a liquid medium of about 20% borate by weight.
19 . The method of claim 10 , wherein the damaged surface of the railroad tie is a vacated spike hole.
20 . The method of claim 10 , further comprising the steps of:
adzing the surface of the railroad tie; and
applying the borate compound and the curable polymer composition to the adzed surface.
21 . A method for treating railroad ties, comprising:
providing a first borate compound, and a 2-component polyurethane compound comprising an isocyanate and a polyol;
mixing the first borate compound and the polyol;
preparing the polyurethane compound from the mixture of the first borate compound and the polyol and the isocyanate;
applying a second borate compound to the railroad tie;
applying the polyurethane compound to the railroad tie;
curing the polyurethane compound.
22 . The method of claim 21 , wherein the borate compound is mixed into the polyol in an amount of about 2.5% borate by weight
23 . The method of claim 21 , wherein the polyurethane compound is prepared as a 1:1 ratio by volume of isocyanate and polyol.
24 . The method of claim 21 , wherein the second borate compound comprises about 30% borate by weight in a liquid medium.