Liquid crystal polyester resin composition for camera module
View Patent ↗A resin composition for surface-mountable (SMT) camera modules which is excellent in the balance between heat resistance, rigidity, strength or moldability and surface exfoliation characteristics is provided by using a liquid-crystal polyester resin composition which comprises 100 parts by mass of a liquid-crystal polyester, 15 to 60 parts by mass of talc having a number-mean particle diameter of 10 to 50 μm, 25 to 50 parts by mass of glass fiber having a number-mean fiber length of 100 to 200 μm, 6 to 20 parts by mass of titanium oxide, and 2 to 10 parts by mass of carbon black and which exhibits a melt viscosity of 10 to 100 Pa S as determined at a shear rate of 100 sec −1 and 370° C. and a deflection temperature under load of 220° C. or above.
1. A liquid crystal polyester resin composition for a camera module, characterized by comprising, based on 100 parts by mass of a liquid crystal polyester, 50 to 110 parts by mass of talc having a number average particle size of 10 to 50 μm, and 2 to 10 parts by mass of carbon black, wherein a deflection temperature under load is 220° C. or more and a melt viscosity at a shear rate of 100 sec −1 at 370° C. is 10 to 150 Pa·S.
2. The liquid crystal polyester resin composition according to claim 1 , characterized in that a number of exfoliations from a surface of a molded article by injection molding according to the following definition is 200 or less,
number of exfoliations=number of particles in 10 mL of pure water having a maximum diameter in the range of 2 μm or more after subjecting 2 cylindrical injection molded articles having a threaded structure with a 0.3 mm pitch and a 0.2 mm groove depth on an inner side of a 7 mm (outer diameter)×6 mm (inner diameter)×4 mm (height) cylinder to ultrasonic cleaning for 30 seconds at a power of 40 kHz and 480 W in 266 mL of pure water.
3. A liquid crystal polyester resin composition for a camera module, characterized by comprising, based on 100 parts by mass of a liquid crystal polyester, 15 to 60 parts by mass of talc having a number average particle size of 10 to 50 μm, 25 to 50 parts by mass of a glass fiber having a number average fiber length of 100 to 200 μm, and 2 to 10 parts by mass of carbon black, wherein a deflection temperature under load is 220° C. or more and a melt viscosity at a shear rate of 100 sec −1 at 370° C. is 10 to 100 Pa·S.
4. The liquid crystal polyester resin composition according to claim 3 , characterized in that the number of exfoliations from a surface of a molded article by injection molding according to the definition is 280 or less.
5. The liquid crystal polyester resin composition for a camera module according to claim 3 , characterized by further comprising, based on 100 parts by mass of the liquid crystal polyester, 6 to 20 parts by mass of titanium oxide.
6. The liquid crystal polyester resin composition according to claim 5 , characterized in that the number of exfoliations from a surface of a molded article by injection molding according to the definition is 250 or less.
7. The liquid crystal polyester resin composition according to claim 3 , characterized in that a weld strength of a molded article by injection molding is 30 MPa or more.
8. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 1 , by injection molding.
9. The liquid crystal polyester resin composition according to claim 4 , characterized in that a weld strength of a molded article by injection molding is 30 MPa or more.
10. The liquid crystal polyester resin composition according to claim 5 , characterized in that a weld strength of a molded article by injection molding is 30 MPa or more.
11. The liquid crystal polyester resin composition according to claim 6 , characterized in that a weld strength of a molded article by injection molding is 30 MPa or more.
12. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 2 , by injection molding.
13. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 3 , by injection molding.
14. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 4 , by injection molding.
15. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 5 , by injection molding.
16. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 6 , by injection molding.
17. A part for a camera module produced from the liquid crystal polyester resin composition according to claim 7 , by injection molding.