Work piece with a hard film of AlCr-containing material, and process for its production
View Patent ↗A work piece or structural component is coated with a system of film layers at least one of which is composed of (Al y Cr 1-y )X, where X=N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO or CBNO and 0.2≦y<0.7, with the composition within said film being either essentially constant or varying over the thickness of the film continually or in steps, as well as a process for producing it.
1. PVD process for depositing at least one (Al y Cr 1-y )X film on a work piece, where X=N, C, B, CN, BN, CBM, NO, CO, BO, CNO, BNO, CBNO and 0.415≦y≦0.695, comprising the steps of installing at least one work piece in a vacuum coating system with at least one Al z Cr 1-z target, where 0.25≦z<0.75, operating said system at a pressure of 0.5 to 8 Pa with the addition of a nitrogen-, carbon-boron- or oxygen-containing reactive gas and applying on the work piece of a substrate voltage of between −3 and −150V, as an arc of sputtering source, wherein the constituent composition within the said at least one (Al y Cr 1-y )X film is either essentially constant or varies either continuously or in steps over the thickness of the film, said at least one (Al y Cr 1-y )X film having a cubic crystal structure and a rate of wear less than or equal to 1.5×10 −15 m 3 m −1 n −1 , said work piece being selected from among the following tools: a milling tool, a hob, (spherical-head) ball nose mill, planar or profiling cutter, a clearing tool, reamer, (indexable tip) insert for turning and milling, a die, an injection mold or a machine component.
2. PVD process as in claim 1 , wherein X=N and the reactive gas is nitrogen or oxygen.
3. PVD process as in claim 1 , wherein the substrate voltage is pulsed.
4. PVD process as in claim 1 , wherein the Al z Cr 1-z target is a powder-metallurgically produced target.
5. PVD process as in claim 4 , wherein the target is produced by cold-pressing starting material in powder form with repeated subsequent reshaping, at temperatures under 660° C., densification by fluxing and cold fusion, and transformation into its final state with a theoretical density at about 96 to 100%.
6. Process comprising the steps of machining a material with a tool coated with a system of film layers comprising at least one film composed of (Al y Cr 1-y )X, where X=N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO or CBNO and 0.415≦y≦0.695, with the composition within said (Al y Cr 1-y )X film being either essentially constant or varying over the thickness of the (Al y Cr 1-y )X film continually or in steps, said (Al y Cr 1-y )X film having a cubic crystal structure and a rate of wear less than or equal to 1.5×10 −15 m 3 m −1 N −1 , said tool constituting one of the following: a milling tool, a hob, (spherical-head) ball nose mill, planar or profiling cutter, a clearing tool, reamer, (indexable tip) insert for turning and milling, a die or an injection mold, wherein said machining using said tool is performed without the addition of lubricants or cooling agents.
7. Process as in claim 6 , wherein the tool is a hard-metal or HSS hob (cutter) and the cutting speed is 60 to 450 m/min.
8. Process as in claim 6 , wherein the tool is an end-milling, (spherical-head) ball-nose-mill or a roughing cutter.