Vacuum processing chamber manufactured by aluminum casting
The present invention provides a method for manufacturing a vacuum processing chamber comprising a volume which is defined by a wall and which can be evacuated, said wall being made of aluminum by casting, said wall comprising an outer face and an inner face, said inner face faces the volume, and a method for improving the inner face of the wall of a vacuum processing chamber, wherein the inner face of said wall is smoothened by grinding and is subsequently pearl-blasted or shot-blasted. Vacuum processing chambers obtained by said methods are provided too.
1. A method for manufacturing a vacuum processing chamber comprising a volume which is defined by a wall and which can be evacuated, said wall being made of aluminum by casting, said wall comprising an outer face and an inner face, said inner face faces the volume, said method comprises
smoothening the inner surface of said wall by grinding, and subsequent
pearl-blasting or shot-blasting, wherein
the pearls or shots for use in the pearl-blasting or shot-blasting have a diameter of 200 μm to 300 μm.
2. The method according to claim 1 , wherein the pearls or shots for use in the pearl-blasting or shot-blasting are made of a material that is selected from the group consisting of glass, ceramic, glass-ceramic, aluminum oxide and fibre compounds.
3. The method according to claim 1 , wherein a blasting system is used for the pearl-blasting or shot-blasting, said blasting system comprising a jet nozzle having a calibre of between 5 to 8 mm.
4. The method according to claim 1 , wherein the jet pressure for the pearl-blasting or shot-blasting is between 3 to 6 bar.
5. The method according to claim 1 , wherein the distance between the jet nozzle and the surface of the inner face to be shot-blasted or pearl-blasted should be between 300 mm and 500 mm during shot-blasting or pearl-blasting.
6. A method for improving an inner face of a wall of a vacuum processing chamber, said vacuum processing chamber comprising a volume which is defined by the wall, said wall being made of aluminum by casting, said wall comprising an outer face and the inner face, said inner face facing the volume, said method comprises
smoothening the inner face of said wall by grinding, and subsequent
pearl-blasting or shot-blasting, wherein
the inner face of said wall is smoothened by the grinding and the subsequent pearl-blasting or shot-blasting, and wherein
the pearls or shots for use in the pearl-blasting or shot-blasting have a diameter of 200 μm to 300 μm.
7. The method according to claim 6 , wherein a blasting system is used for the pearl-blasting or shot-blasting, said blasting system comprising a jet nozzle having a calibre of between 5 to 8 mm.
8. The method according to claim 6 , wherein the jet pressure for the pearl-blasting or shot-blasting is between 3 to 6 bar.
9. The method according to claim 6 , wherein the distance between the jet nozzle and the surface of the aluminum cast to be shot-blasted or pearl-blasted being between 300 mm and 500 mm during shot-blasting or pearl-blasting.