Polycarbonate resin composition with good light stability and dimensional stability

1. A polycarbonate resin composition comprising:

(A) 70 to 95 parts by weight of a thermoplastic polycarbonate resin;

(B) 5 to 40 parts by weight of a thermoplastic non-crystalline polyester copolymer, wherein the polyester copolymer (B) is a polyalkylene terephthalate copolymer resin comprising an alkylene glycol component which is partially substituted with a cycloalkane dialcohol;

(C) 5 to 50 parts by weight of titanium dioxide;

(D) 0.1 to 10 parts by weight of an organic siloxane polymer; and

(E) 0.05 to 5 parts by weight of a fluorinated polyolefin-based resin.

2. The polycarbonate resin composition of claim 1 , wherein the polyester copolymer (B) is a polyalkylene terephthalate copolymer resin comprising an alkylene glycol component which is partially substituted by 3 to 48 mol % of a cycloalkane dialcohol represented by the following Chemical Formula 2:

HO—(R 3 ) n 3 -A 2 -(R 4 ) n 4 -OH  [Chemical Formula 2]

wherein, in the above Chemical Formula 2, A 2 is cycloalkylene, R 3 and R 4 are independently substituted or unsubstituted alkylene, and n3 and n4 are independently integers ranging from 1 to 4.

3. The polycarbonate resin composition of claim 2 , wherein the polyester copolymer (B) is a polyalkylene terephthalate copolymer resin comprising an alkylene glycol component which is partially substituted by 5 to 20 mol % of a cycloalkane dialcohol represented by Chemical Formula 2.

4. The polycarbonate resin composition of claim 2 , wherein polyester copolymer (B) is a polyethylene terephthalate copolymer resin comprising an ethylene glycol component which is partially substituted by 3 to 48 mol % of 1,4-cyclohexane dimethanol (CHDM) represented by the following Chemical Formula 3.

5. The polycarbonate resin composition of claim 1 , comprising 10 to 30 parts by weight of said non-crystalline polyester copolymer (B).

6. The polycarbonate resin composition of claim 1 , wherein the titanium dioxide is surface-treated with a surface treatment agent comprising an inorganic surface treatment agent, an organic surface treatment agent, or a combination thereof.

7. The polycarbonate resin composition of claim 6 , wherein the inorganic surface treatment agent comprises silicon dioxide, zirconium dioxide, sodium silicate, sodium aluminate, sodium aluminum silicate, mica, or a combination thereof; the organic surface treatment agent comprises polydimethylsiloxane, trimethylpropane (TMP), pentaerythritol, or a combination thereof; and the titanium dioxide comprises said inorganic surface treatment agent, organic surface treatment agent, or combination thereof in an amount of 0.3 parts by weight or less based on 100 parts by weight of the titanium dioxide.

8. The polycarbonate resin composition of claim 1 , comprising 10 to 30 parts by weight of said titanium dioxide (C).

9. The polycarbonate resin composition of claim 1 , wherein the organic siloxane polymer (D) comprises a compound represented by the following Chemical Formula 4:

wherein, in the above Chemical Formula 4, R 11 and R 12 are independently alkyl or aryl, R 21 to R 27 are independently alkyl, aryl, hydroxy, alkoxy, aryloxy, or alkenyl, Ar is aryl, n and m are integers representing a repeating unit, and n+m ranges from 1 to 500.

10. The polycarbonate resin composition of claim 9 , wherein the organic siloxane polymer (D) comprises a phenyl-substituted siloxane copolymer represented by the following Chemical Formula 5.

wherein R 11 and R 12 are independently methyl or phenyl, R 21 to R 27 are independently methyl, phenyl, hydroxy, methoxy, ethoxy, phenoxy, or vinyl, and n and m are the same as in Chemical Formula 4.

11. The polycarbonate resin composition of claim 9 , wherein the organic siloxane polymer comprises poly(methylphenyl)siloxane, poly(diphenyl)siloxane, dimethylsiloxane-diphenylsiloxane, a dimethylsiloxane-methylphenylsiloxane copolymer, or a combination thereof.

12. The polycarbonate resin composition of claim 9 , wherein the organic siloxane copolymer has a dynamic viscosity of 1 to 1000 mm 2 /S at 25° C.

13. The polycarbonate resin composition of claim 1 , wherein the fluorinated polyolefin-based resin (E) comprises polytetrafluoroethylene, polyvinylidenefluoride, a tetrafluoroethylene/vinylidenefluoride copolymer, a tetrafluoroethylene/hexafluoropropylene copolymer, an ethylene/tetrafluoroethylene copolymer, or a mixture thereof.

14. The polycarbonate resin composition of claim 1 , wherein the polycarbonate resin composition further comprises an additive comprising an ultraviolet (UV) stabilizer, a fluorescent whitening agent, a lubricant, a release agent, a nuclear agent, an antistatic agent, a stabilizer, a reinforcing material, an inorganic material additive, a pigment, a dye, or a mixture thereof in an amount of 60 parts by weight or less based on 100 parts by weight of the polycarbonate resin.

15. A molded product made using the polycarbonate resin composition according to claim 1 .