Separator, battery using the same, method for producing separator, microporous membrane, and method for producing a microporous membrane
A separator includes a porous body, and a particle membrane that is formed on at least one principal surface of the porous body. The particle membrane is made of inorganic particles, and has a void formed therein by the inorganic particles. The particle membrane has a porosity that is non-uniform in the thickness direction thereof.
1. A separator comprising:
a porous body; and
a particle membrane that is formed on at least one principal surface of the porous body, is made of inorganic particles by a vapor deposition process, and has a void formed therein by the inorganic particles,
wherein the particle membrane has a porosity that is non-uniform in a thickness direction thereof, wherein at least 50% of the inorganic particles have a secondary particle diameter of 20 nm or less,
wherein the particle membrane has an oxidation degree that is non-uniform in a thickness direction thereof such that the oxidation degree is operably controllable by supplying oxygen gas to the principal surface of the porous body during vapor deposition of the inorganic particle membrane,
wherein (1) the oxidation degree is highest near an outer surface of the particle membrane and lowest near an interface between the particle membrane and the porous body, or (2) the oxidation degree is lowest near the outer surface of the particle membrane and highest near the interface between the particle membrane and the porous body, and
wherein the particle membrane has a thickness of 10 nm or more and less than 100 nm.
2. A separator according to claim 1 , wherein the porosity is set so that, in the thickness direction of the particle membrane, it is highest near an interface between the particle membrane and the porous body.
3. A separator according to claim 2 , wherein the porosity is set so that, in the thickness direction of the particle membrane, it is lowest near an outer surface of the particle membrane.
4. A separator according to claim 3 , wherein the porosity is set so that, in the thickness direction of the particle membrane, it gradually decreases from the interface between the particle membrane and the porous body to the outer surface of the particle membrane.
5. A separator according to claim 1 , wherein
the porous body is an organic polymer porous body made of an organic polymer material.
6. A separator according to claim 5 , wherein the organic polymer material is a polyolefin-based resin, a polyimide-based resin, or a polyamide-based resin.
7. A separator according to claim 1 , wherein the particle membrane is formed on each principal surface of the porous body.
8. A battery comprising:
a positive electrode;
a negative electrode; and
a separator according to claim 1 .
9. A microporous membrane comprising:
a porous body; and
a particle membrane that is formed on at least one principal surface of the porous body, is made of inorganic particles by a vapor deposition process, and has a void formed therein by the inorganic particles,
wherein the particle membrane has a porosity that is non-uniform in a thickness direction thereof, wherein at least 50% of the inorganic particles have a secondary particle diameter of 20 nm or less,
wherein the particle membrane has an oxidation degree that is non-uniform in a thickness direction thereof such that the oxidation degree is operably controllable by supplying oxygen gas to the principal surface of the porous body during vapor deposition of the inorganic particle membrane,
wherein (1) the oxidation degree is highest near an outer surface of the particle membrane and lowest near an interface between the particle membrane and the porous body, or (2) the oxidation degree is lowest near the outer surface of the particle membrane and highest near the interface between the particle membrane and the porous body, and
wherein the particle membrane has a thickness of 10 nm or more and less than 100 nm.
10. A separator according to claim 1 , wherein the density of the inorganic particles is set so that, in the thickness direction of the particle membrane, it gradually decreases from an outer surface of the inorganic particle membrane to an interface between the particle membrane and the porous body.
11. A battery according to claim 8 , wherein the density of the inorganic particles is set so that, in the thickness direction of the particle membrane, it gradually decreases from an outer surface of the inorganic particle membrane to an interface between the particle membrane and the porous body.
12. A microporous membrane according to claim 9 , wherein the density of the inorganic particles is set so that, in the thickness direction of the particle membrane, it gradually decreases from an outer surface of the inorganic particle membrane to an interface between the particle membrane and the porous body.
13. A separator according to claim 1 , wherein the lowest porosity of the particle membrane is about 40% or less.
14. A battery according to claim 8 , wherein the lowest porosity of the particle membrane is about 40% or less.
15. A microporous membrane according to claim 9 , wherein the lowest porosity of the particle membrane is about 40% or less.