Catalytic platinum and its 3d-transition-metal alloy nanoparticles
View Patent ↗Platinum (Pt)-based alloys are effective catalysts for oxygen reduction reaction (ORR) or fuel oxidation in proton exchange membrane fuel cells (PEMFCs). A wet-chemical approach for preparing monodisperse Pt 3 Ni, Pt 3 Co and Pt 3 Fe nanocubes and Pt 3 Ni nanoctahedra which are terminated with {100} and {111} facets, respectively, were developed. Such nanoscaled electrocatalysts supported on carbon black with controlled shape, e.g., octahedral configuration, is provided. ORR activity on the Pt 3 Ni nanoctahedra is ˜5.1 fold higher than that of nanocubes with a similar size, and their C-supported samples are highly active with respect to commercial Pt/C.
1. Catalytic particles, comprising:
nano-particles presenting a plurality of facets having catalytic activity with respect to at least an oxidation-reduction reaction, formed by a process comprising:
heating and mixing an organic solution comprising a soluble platinum salt, a set of capping agents having a reducing potential sufficient to reduce the soluble platinum salt, and having surface active properties to lower a surface energy on facets of particles formed from the reduced platinum salt, and a shape control agent comprising a compound of a metal other than platinum, to selectively control a shape of the formed particles to provide at least one {111} terminated facet on each nano-particle; and
separating formed particles from the solution.
2. The catalytic particles according to claim 1 , wherein the soluble platinum salt is platinum (II) acetylacetonate.
3. The catalytic particles according to claim 1 , wherein the process further comprises adding a soluble transition metal salt to the organic solvent, wherein the formed particles comprise an alloy of platinum and the transition metal.
4. The catalytic particles according to claim 3 , wherein the transition metal salt comprises nickel.
5. The catalytic particles according to claim 3 , wherein the transition metal salt is nickel (II) acetylacetonate.
6. The catalytic particles according to claim 3 , wherein the transition metal salt comprises at least one of copper (II) chloride, bromide, and iodide, and wherein the formed particles comprise PtCu.
7. The catalytic particles according to claim 1 , wherein the process is conducted under anoxic conditions.
8. The catalytic particles according to claim 1 , wherein the shape control agent comprises Tungsten hexacarbonyl.
9. The catalytic particles according to claim 1 , wherein the shape control agent comprises molybdenum hexacarbonyl.
10. The catalytic particles according to claim 1 , wherein the shape control agent comprises chromium hexacarbonyl.
11. The catalytic particles according to claim 1 , wherein the process comprises heating the solvent to a temperature of about 170 C to 240 C.
12. The catalytic particles according to claim 1 , wherein the process further comprises resuspending the formed particles in a non-polar organic solvent.
13. The catalytic particles according to claim 1 , wherein the formed particles are substantially monodisperse nanopolyhedra.
14. The catalytic particles according to claim 1 , wherein the organic solution comprises oleylamine and oleic acid.
15. The catalytic particles according to claim 1 , wherein the process further comprises adding a soluble transition metal salt to the organic solution, wherein:
the formed particles comprise an alloy of platinum and the transition metal;
the soluble platinum salt comprises platinum (II) acetylacetonate;
the organic solution comprises oleylamine and oleic acid;
the shape control agent comprises tungsten hexacarbonyl; and
the formed particles are substantially monodisperse nanoctahedral catalytic particles.
16. The catalytic particles according to claim 15 , wherein the transition metal salt comprises nickel (II) acetylacetonate, and wherein the formed particles comprise Pt 3 Ni 1 .
17. Monodisperse nanopolyhedric catalytic particles, formed by a process comprising:
heating and mixing a soluble platinum salt in an organic solution comprising a set of capping agents having a reducing potential sufficient to reduce the platinum salt, and having surface active properties to lower a surface energy on facets of formed particles, wherein the formed particles each have at least one {111} terminated facet;
adding a shape control agent comprising a metal other than platinum, to selectively control a particle shape; and
separating the formed particles from the solution.
18. The particles according to claim 17 , wherein the particles are formed by a process further comprising adding a soluble transition metal salt to the organic solvent, wherein the formed particles comprise an alloy of platinum and the transition metal, wherein the transition metal salt comprises at least one of nickel, cobalt and copper, and wherein the shape control agent comprises at least one of Tungsten hexacarbonyl, molybdenum hexacarbonyl, and chromium hexacarbonyl.
19. The particles according to claim 17 , wherein the organic solution comprises oleylamine and oleic acid.
20. The particles according to claim 17 , wherein the particle is formed by a process further comprising adding a soluble transition metal salt to the organic solution, wherein:
the formed particles comprise an alloy of platinum and the transition metal;
the soluble platinum salt comprises platinum (II) acetylacetonate;
the organic solution comprises oleylamine and oleic acid;
the shape control agent comprises tungsten hexacarbonyl; and
the formed particles are substantially monodisperse nanoctahedral catalytic particles.
21. The particles according to claim 17 , wherein the transition metal salt comprises nickel, the transition metal salt is nickel (II) acetylacetonate, and the formed particles comprise Pt 3 Ni 1 .
22. The particles according to claim 17 , wherein the transition metal salt comprises copper, the transition metal salt is at least one of copper (II) chloride, bromide, and iodide, and the formed particles comprise PtCu.
23. Monodisperse nanopolyhedric crystalline catalytic particles comprising a platinum-transition metal alloy, having a nanocubic or a nanooctahedric configuration having at least one {111} terminated facet, configured to catalyze at least an oxidation reduction reaction of a direct methanol fuel cell with greater resistance to carbon monoxide poisoning than a pure platinum metal particle catalyst particle having the same surface area.