Catalytic platinum-copper alloy nanoparticles
View Patent ↗High-quality bimetallic Pt x Cu 100-x (x=54-80 at. %) nanocubes can be prepared from a hot organic solution. Synthetic conditions, such as the ratio of oleylamine/tetraoctylammonium bromide as well as the doses of 1-dodecanethiol and 1,2-tetradecanediol have been optimized to ensure a formation of Pt—Cu nanocubes. Electrochemical evaluation shows that the catalytic activity of Pt 60 Cu 40 nanocubes for methanol oxidation is superior, in comparison with those of spherical Pt 60 Cu 40 nanocubes and Pt nanocubes with similar sizes, implying that the {100}-terminated Pt 60 Cu 40 nanocubes offer a higher activity for methanol oxidation reaction than those with mixed crystallographic facets do. As another example, it was identified that Pt 80 Cu 20 nanocubes is the best electrocatalyst on the basis of the maintainable electrocatalytic activity (which is even slightly superior to that of pure Pt nanocubes) and remarkable long-term stability (˜300 hours vs 3 hours for Pt nanocubes) when being performed towards formic acid oxidation reaction.
1. Catalytic nanocubes, enclosed by {100} facets, formed by a process comprising:
heating in an organic solution, a soluble platinum salt, a transition metal salt comprising copper, and a set of surface active capping agents, the solution having shape control properties to selectively control a particle shape; and
reducing the platinum salt and transition metal salt to form catalytically active platinum alloy nanocubes.
2. The catalytic nanocubes according to claim 1 , wherein the soluble platinum salt is platinum (II) acetylacetonate.
3. The catalytic nanocubes according to claim 1 , wherein the transition metal salt is copper (II) acetylacetonate.
4. The catalytic nanocubes according to claim 1 , wherein the process is conducted under anoxic conditions.
5. The catalytic nanocubes according to claim 1 , wherein the solution comprises a thiol coordination agent.
6. The catalytic nanocubes according to claim 1 , wherein the solution comprises a diol reducing agent.
7. The catalytic nanocubes according to claim 1 , wherein the solvent is heated to about 210° C. to 230° C.
8. The catalytic nanocubes according to claim 1 , wherein the formed particles comprise at least 90% nanocubes.
9. The catalytic nanocubes according to claim 1 , wherein the formed particles are substantially monodisperse.
10. The catalytic nanocubes according to claim 1 , wherein:
the surface active capping agent comprises tetraoctylammonium bromide;
the soluble platinum salt comprises platinum (II) acetylacetonate;
the transition metal salt comprises copper (II) acetylacetonate; and
the platinum salt and transition metal salt are reduced by at least one of an amine and a diol.
11. Substantially monodisperse nanocube alloy particles enclosed by {100} facets, formed by a process comprising:
heating in an organic solution, a soluble platinum salt, a transition metal salt comprising copper, and a set of surface active capping agents, the solution having shape control properties to selectively control a particle shape; and
reducing the platinum salt and transition metal salt to form catalytically active platinum alloy nanocubes.
12. The substantially monodisperse catalytic nanocubes according to claim 11 , wherein the soluble platinum salt is platinum (II) acetylacetonate and the transition metal salt is copper (II) acetylacetonate.
13. The substantially monodisperse catalytic nanocubes according to claim 11 , wherein the process is conducted under anoxic conditions.
14. The substantially monodisperse catalytic nanocubes according to claim 11 , wherein the solution comprises a thiol coordination agent.
15. The substantially monodisperse catalytic nanocubes according to claim 11 , wherein the solution comprises a diol reducing agent.
16. The substantially monodisperse catalytic nanocubes according to claim 11 , wherein the solvent is heated to about 210° C. to 230° C.
17. The substantially monodisperse catalytic nanocubes according to claim 11 , wherein:
the solution is heated to about 210° C. to 230° C. under anoxic conditions;
the solution further comprises a thiol coordination agent;
the surface active capping agent comprises tetraoctylammonium bromide;
the soluble platinum salt comprises platinum (II) acetylacetonate;
the transition metal salt comprises copper (II) acetylacetonate; and
the platinum salt and transition metal salt are reduced by at least one of an amine and a diol.
18. Substantially monodisperse nanocube alloy particles according to claim 11 , wherein:
the surface active capping agent comprises tetraoctylammonium bromide;
the soluble platinum salt comprises platinum (II) acetylacetonate;
the transition metal salt comprises copper (II) acetylacetonate; and
the platinum salt and transition metal salt are reduced by at least one of an amine and a diol reducing agent.
19. Substantially monodisperse nanocube alloy particles according to claim 11 , wherein the solution has shape control properties to selectively control a particle shape to form cubic particles, and the platinum salt and transition metal salt are reduced with a chemical reducing potential to form the catalytically active platinum alloy nanocubes.