Cementitious compositions
View Patent ↗The invention provides a cementitious composition comprising a cement component comprising (i) an accelerant, (ii) a calcium sulphate source and (iii) an ettringite forming cement; an aggregate; and optionally water; wherein the cement has a minimum unconfined compressive strength of 1500 psi when tested in accordance with ASTM C1140 and/or C1604 at 15 minutes after placement; methods for its use and concrete formed from it.
1. A gunite forming composition consisting of:
(a) a dry cement component which consists of (i) a nucleation agent accelerant, (ii) a calcium sulphate source selected from the group consisting of beta anhydrite, gypsum and hemi-hydrate, and (iii) from 30% by weight of calcium sulphoaluminate as an ettringite forming cement, and
(b) an aggregate, wherein
the weight ratio of the aggregate (b) to the cement component (a) is from about 2:1 to about 6:1, and wherein
when the composition is mixed with water, the resulting mixture has undergone final set and hardened sufficiently to possess a minimum unconfined compressive strength of 1500 psi when tested in accordance with ASTM C1140 and/or C1604 at 15 minutes after placement.
2. A composition as defined in claim 1 wherein the ettringite forming cement further consists of a mixture of a high alumina cement and calcium sulphate.
3. A composition as defined in claim 1 wherein the ettringite forming cement is present in an amount from 30% by weight to 80% by weight; the accelerant is present in an amount from about 0.01% by weight to about 5% by weight; and the calcium sulphate source is present in an amount from about 1% by weight to about 70% by weight.
4. A composition as defined in claim 1 which is sprayable.
5. A composition as defined in claim 1 , wherein water when present in the composition is in a water to cement solids weight ratio of from about 0.25:1 to about 0.8:1.
6. A composition as defined in claim 1 , wherein the composition has a minimum unconfined compressive strength of 5000 psi.
7. A composition as defined in claim 1 , wherein the composition has a minimum unconfined compressive strength of 6000 psi.
8. A method of applying a cementitious composition to a surface which method comprises the steps of (i) providing a composition according to claim 1 ; and (ii) applying the composition to the surface.
9. A method as defined in claim 8 wherein the surface to which the composition is applied is a mine, tunnel or building structure surface.
10. A method as defined in claim 8 wherein the composition comprises water, wherein the water is present in the composition in a water to cement solids weight ratio of from about 0.25:1 to about 0.8:1.
11. A method of applying a cementitious composition to a surface which method comprises the steps of (i) a composition according to claim 1 ; (ii) mixing the composition with water; and (ii) applying the mixed composition to the surface.
12. A method as defined in claim 11 wherein the surface to which the composition is applied is a mine, tunnel or building structure surface.
13. A method as defined in claim 11 wherein step (ii) of the method comprises supplying water in a water to cement solids weight ratio of from about 0.25:1 to about 0.8:1.
14. A composition as defined in claim 1 wherein when the composition is mixed with water, the resulting mixture has undergone final set and hardened sufficiently to possess a minimum unconfined compressive strength of 1500 psi when tested in accordance with ASTM C1140 and/or C1604 at 15 minutes after placement.