EVA blend compositions suitable for RF welding applications
View Patent ↗Disclosed are films obtained from blends of ethylene copolymers with organic acid salt-modified potassium ionomeric copolymers. The films of the present invention can be welded using RF energy.
1. A multilayer film having a thickness of at least about 0.001 mil to about 25 mil that absorbs radio frequency energy comprising
A. a first layer consisting essentially of
1. a first component comprising a mixture of
a. at least one polymer selected from the group consisting of E/X/Y copolymers, ionomers of E/X/Y copolymers and mixtures thereof, where E is ethylene, X is a C 3 to C 8 α,β-ethylenically unsaturated carboxylic acid and Y is a comonomer selected from the group consisting of alkyl acrylates and alkyl methacrylates having alkyl groups of from one to eight carbon atoms, wherein said E/X/Y copolymers comprise from about 2-30 weight %, based on the weight of the E/X/Y copolymer, of copolymerized units of X and from about 0-40 weight %, based on the weight of the E/X/Y copolymer, of copolymerized units of Y, and
b. a material selected from the group consisting of organic carboxylic acids having from about 6 to about 38 carbon atoms, salts of said organic carboxylic acids and mixtures thereof;
wherein the combined carboxylic acid groups present in said polymer and said material of said first component are neutralized to a level of at least 70% by potassium ions; and
2. a second component in an amount of from about 50 to about 95 wt. %, based on the total weight of said first and second components, wherein said second component is different from said at least one polymer of said first component and is selected from the group consisting of ethylene vinyl acetate copolymers, ethylene carbon monoxide copolymers, ethylene vinyl alcohol copolymers and mixtures thereof; and
B. at least one additional film layer.
2. The film of claim 1 wherein the second component of the first layer is present in an amount of from about 70 to about 93 wt %, based on the total weight of the first and second components.
3. The film of claim 1 wherein the first component of the first layer comprises a mixture of a first ionomer of an E/X/Y copolymer and at least one additional ionomer of an E/X/Y copolymer that is different from said first ionomer.
4. The film of claim 1 wherein the second component of the first layer is an ethylene vinyl acetate copolymer.
5. The film of claim 1 wherein the second component of the first layer is an ethylene carbon monoxide copolymer.
6. The film of claim 1 wherein the second component of the first layer is an ethylene vinyl alcohol copolymer.
7. The film of claim 1 wherein the combined carboxylic acid groups present in said polymer and said material of said first component of the first layer are neutralized solely by potassium ions.
8. A film of claim 1 having a thickness of about 6 mil to about 12 mil.
9. An article selected from the group consisting of film wraps, containers and lids, wherein said article comprises a multilayer film as recited in claim 1 .
10. A film wrap of claim 9 .