Method of fabricating an improved mold core and a mold core obtained by said method
View Patent ↗The present invention relates to a method of fabricating a mold core ( 5 ) for making hollow parts ( 11 ) based on a composite material including fibers, fabrics, or textiles together with a resin, the method consisting in mixing a filler material ( 1 ) and a binder material ( 2 ) in order to obtain a uniform mixture of materials, and in solidifying, compacting, and shaping the resulting mixture in order to constitute said core, the method being characterized in that it further consists in introducing into the mixture at least one complementary material ( 3 ) that is expandable under the effect of heat or by applying another physical or chemical principle, and in mixing said materials ( 1, 2, 3 ) in order to obtain a uniform distribution of the complementary material ( 3 ) in the mixture.
1. A method of fabricating a mold core for making a composite part which is hollow or has undercuts and which is based on a composite material including fibers, fabrics, or textiles together with a resin, the method comprising mixing a filler material having a grain size between 10 μm and 2 mm with a binder material and at least one complementary material comprising expandable graphite particles in order to obtain a uniform mixture, the expandable graphite particles being expandable under the effect of heat, wherein at least one of the filler material and the binder material is liquid soluble; and solidifying, compacting, and shaping the uniform mixture to at least partly surround an insoluble kernel in order to constitute said core, wherein the mixture comprises an amount of said graphite particles determined as a function of a desired volume expansion percentage of said mold core for a given temperature difference in a certain temperature range, wherein said amount lies between 0.01% to 99.99% of the total combined weight of the uniform mixture, and wherein said mold core expands while making said composite part so as to exhibit self-sealing and self-healing properties.
2. The method according to claim 1 , wherein the filler, binder, and complementary materials are in powder or granular form.
3. The method according to claim 1 , wherein at least one of the filler material and the binder material is water soluble.
4. The method according to claim 1 , wherein said grain size is between 201 μm and 2 mm, and wherein said amount of the expandable graphite particles lies between 20% to 99.99% of the total combined weight of the uniform mixture.
5. A method of making a hollow composite part based on a composite material including fibers, fabrics, or textiles together with a resin, the method comprising mixing a filler material having a grain size between 10 μm and 2 mm with a binder material and expandable graphite particles in order to obtain a uniform mixture, the expandable graphite particles being expandable under the effect of heat, wherein at least one of the filler material and the binder material is liquid soluble; solidifying, compacting, and shaping the mixture to at least partly surround an insoluble kernel in order to form a mold core; molding said composite material around the core; and exposing the core to a liquid which dissolves at least a portion thereof in order to form said hollow part, wherein the mixture comprises an amount of said graphite particles determined as a function of a desired volume expansion percentage of said mold core for a given temperature difference in a certain temperature range, and wherein said mold core expands during said molding so as to exhibit self-sealing and self-healing properties.
6. A method of fabricating a mold core for making a hollow composite part based on a composite material including fibers, fabrics, or textiles together with a resin, the method comprising:
mixing a filler material having a grain size between 10 μm and 2 mm with a binder material and expandable graphite particles in order to obtain a uniform mixture; and
shaping and solidifying the uniform mixture to at least partly surround an insoluble kernel in order to form said mold core, the expandable graphite particles being expandable under the effect of heat, and at least one of the filler material and the binder material being liquid soluble so that said composite material can be molded about the mold core with at least a portion of the mold core subsequently being removed via exposure thereof to said liquid in order to form said hollow part,
wherein the mixture comprises an amount of said graphite particles determined as a function of a desired volume expansion percentage of said mold core for a given temperature difference in a certain temperature range,
wherein said amount lies between 0.01% to 99.99% of the total combined weight of the uniform mixture, and
wherein said mold core expands while making said composite part so as to exhibit self-sealing and self-healing properties.
7. The method according to claim 6 , wherein at least one of the filler material and the binder material is water soluble.
8. The method according to claim 6 , wherein said grain size is between 201 μm and 2 mm, and wherein said amount of the expandable graphite particles lies between 20% to 99.99% of the total combined weight of the uniform mixture.
9. The method according to claim 6 , wherein said volume expansion allows for a compensation of any de-bulking movement of the composite material or any thermal expansion movement of outer mold tooling during molding, and wherein said volume expansion exerts pressure on the composite material to compensate for hydrostatic pressure within the part or for additional compaction thereof during molding.