Method of fabricating a friction part based on C/C composite material
View Patent ↗The carbon-carbon composite material is obtained by densification with a pyrolytic carbon matrix originating from a precursor in gaseous state at least in a main external phase of the matrix, and, at the end of the densification, final heat treatment is performed at a temperature lying in the range 1400° C. to 1800° C.
1. A method of fabricating a friction part based on carbon/carbon composite material formed of a fiber reinforcement and a carbon matrix, the method comprising:
making a preform of carbon precursor fibers and transforming the preform into a carbon fiber preform using a carbonization heat treatment at a temperature in the range 750° C. to 1100° C.;
treating the carbon fiber preform in an inert atmosphere at a temperature between 1600° C. and 2500° C.;
densifying the preform with pyrolytic carbon originating from a precursor in gaseous state to form the whole carbon matrix with said pyrolytic carbon at a temperature between 850° C. and 1050° C. and at a pressure between 0.5 kPa and 3.3 kPa; and
following said densification performing a final heat treatment at a temperature lying in the range 1400° C. to 1800° C. without inducing graphitization of said carbon matrix.
2. A method according to claim 1 , wherein the final heat treatment is performed at a temperature lying in the range 1550° C. to 1700° C.
3. A method according to claim 1 , wherein the pyrolytic carbon matrix is formed of a rough laminar type.
4. A method according to claim 1 , wherein the fiber preform is made by superposing two-dimensional fiber plies made of carbon precursor fibers, bonding the plies together by needling progressively as plies are superposed, and carbonizing to transform the carbon precursor fibers into carbon fibers.
5. A method according to claim 4 , wherein the needling of each newly superposed ply is performed with a needling density of no more than 90 strokes/cm 2 .
6. A method of fabricating a friction part based on carbon/carbon composite material formed of a fiber reinforcement and a carbon matrix, the method comprising:
making a preform of carbon precursor fibers and transforming the preform into a carbon fiber preform using a carbonization heat treatment at a temperature in the range 750° C. to 1100° C.;
treating the carbon fiber preform in an inert atmosphere at a temperature between 1600° C. and 2500° C.;
densifying the preform with pyrolytic carbon originating from a precursor in gaseous state to form the whole carbon matrix with said pyrolytic carbon at a temperature between 850° C. and 1050° C. and at a pressure between 0.5 kPa and 3.3 kPa; and
following said densification performing a final heat treatment at a temperature lying in the range 1400° C. to 1800° C., said temperature being below a temperature that induces graphitization of said carbon matrix.
7. A method according to claim 6 , wherein the final heat treatment is performed at a temperature lying in the range 1550° C. to 1700° C.