White persistent phosphor blend or layered structure
View Patent ↗This disclosure features a blend, or use together in at least two layers of an article of manufacture, of a first persistent phosphor, a second persistent phosphor and a third phosphor. The first persistent phosphor has a formula I: Ca x-y-z-a A a Al 2-m-n-o-p O d :Eu y ,RE z ,B m ,Zn n ,Co o ,Sc p I where the variables are defined in the disclosure. The second persistent phosphor has a formula II: Sr x-y-z-a A a Al 14-m-n-o-p O d :Eu y ,RE z ,B m ,Zn n ,Co o ,Sc p II where the variables are defined in the disclosure. The third phosphor is a non-persistent phosphor that is excited at a wavelength in a range of 300-500 nm. Also featured is an article of manufacture including the blend or the phosphors present in at least two layers. Once the blend or layered structure comprising the three phosphors has been excited it can appear white in an absence of ambient light.
1. A blend of a first persistent phosphor, a second persistent phosphor and a third non-persistent phosphor, wherein said first persistent phosphor has a formula I:
Ca x-y-z-a A a Al 2-m-n-o-p O d :Eu y ,RE z ,B m ,Zn n ,Co o ,Sc p I
where x is between 0.75 and 1.3; y is between about 0.0005 and about 0.1; z is between about 0.0005 and about 0.1; a is between about 0 and about 0.2; A is one or both of Sr and Ba; m is between about 0 and about 0.3; n is between about 0 and about 0.1; o is between about 0 and about 0.01; p is between about 0 and about 0.10; RE is any rare earth ion and d ranges from about 3.945 to about 4.075;
wherein said second persistent phosphor has a formula II:
Sr x-y-z-a A a Al 14-m-n-o-p O d :Eu y ,RE z ,B m ,Zn n ,Co o ,Sc p II
where x is between 3.0 and 5.2; y is between about 0.0005 and about 0.1; z is between about 0.0005 and about 0.1; a is between about 0 and about 0.2; A is one or both of Ca and Ba; m is between about 0 and about 0.3; n is between about 0 and about 0.1; o is between about 0 and about 0.01; p is between about 0 and about 0.10; RE is any rare earth ion and d ranges from about 23.945 to about 26.425; and
wherein said third phosphor is a non-persistent phosphor that is excited at a wavelength in a range of 300-500 nm.
2. The phosphor blend of claim 1 wherein RE is at least one of Dy 3+ and Nd 3+ .
3. The phosphor blend of claim 1 wherein said third phosphor is selected from the group consisting of 3.5MgO-0.5MgF 2 —GeO 2 ; Mn +4 (MFG); Y 3 Al 5 O 12 ; Ce (YAG:Ce 3+ ); (Tb, Y, Lu, La, Gd) 3 (Al, Ga) 5 O 12 :Ce 3+ (TAG:Ce); (Ca, Sr) 8 (Mg,Zn)(SiO 4 ) 4 Cl 2 :Eu 2+ , Mn 2+ (CASI) and combinations thereof.
4. The phosphor blend of claim 1 comprising at least one additional phosphor in said blend.
5. The phosphor blend of claim 1 wherein ratios of amounts (in % wt) of said third phosphor, said second persistent phosphor and said first persistent phosphor in said blend are approximately 2-3:2-4:3-5, respectively, with the amounts of said third phosphor, said second phosphor and said first phosphor totaling 100% of the blend by weight.
6. The phosphor blend of claim 5 wherein said ratios are approximately 3:3:4.5.
7. The phosphor blend of claim 5 wherein said ratios are approximately 2.5:3:4.5.
8. The phosphor blend of claim 1 wherein once said blend has been excited said blend appears white in an absence of ambient light.
9. The phosphor blend of claim 1 wherein said formula II of said second persistent phosphor is Sr 4-y-z Al 14 O 25 :Eu 2+ y , Dy 3+ z .
10. The phosphor blend of claim 9 wherein said formula I of first persistent phosphor is Ca 1-y-z Al 2 O 4 :Eu 2+ y , Nd 3+ z .
11. The phosphor blend of claim 10 wherein said third phosphor is selected from the group consisting of 3.5MgO-0.5MgF 2 —GeO 2 ; Mn +4 (MFG); Y 3 Al 5 O 12 ; Ce (YAG:Ce 3+ ); (Tb, Y, Lu, La, Gd) 3 (Al, Ga) 5 O 12 :Ce 3+ (TAG:Ce); (Ca, Sr) 8 (Mg,Zn)(SiO 4 ) 4 Cl 2 :Eu 2+ , Mn 2+ (CASI) and combinations thereof.
12. The phosphor blend of claim 1 wherein said third phosphor is selected from the group consisting of a yellow emitter, a yellow-orange emitter, an orange-red emitter, a red emitter and combinations thereof.
13. An article of manufacture comprising said phosphor blend of claim 1 .
14. An article of manufacture comprising at least two layers having one or more of a first persistent phosphor, a second persistent phosphor and a third phosphor in each of said layers, wherein said first persistent phosphor has a formula I:
Ca x-y-z-a A a Al 2-m-n-o-p O d :Eu y ,RE z ,B m ,Zn n ,Co o ,Sc p I
where x is between 0.75 and 1.3; y is between about 0.0005 and about 0.1; z is between about 0.0005 and about 0.1; a is between about 0 and about 0.2; A is one or both of Sr and Ba; m is between about 0 and about 0.3; n is between about 0 and about 0.1; o is between about 0 and about 0.01; p is between about 0 and about 0.10; RE is any rare earth ion and d ranges from about 3.945 to about 4.075;
wherein said second persistent phosphor has a formula II:
Sr x-y-z-a A a Al 14-m-n-o-p O d :Eu y ,RE z ,B m ,Zn n ,Co o ,Sc p II
where x is between 3.0 and 5.2; y is between about 0.0005 and about 0.1; z is between about 0.0005 and about 0.1; a is between about 0 and about 0.2; A is one or both of Ca and Ba; m is between about 0 and about 0.3; n is between about 0 and about 0.1; o is between about 0 and about 0.01; p is between about 0 and about 0.10; RE is any rare earth ion and d ranges from about 23.945 to about 26.425; and
wherein said third phosphor is a non-persistent phosphor that is excited at a wavelength in a range of 300-500 nm.
15. The article of manufacture of claim 14 wherein RE is at least one of Nd 3+ and Dy 3+ .
16. The article of manufacture of claim 15 wherein said third phosphor is selected from the group consisting of 3.5MgO-0.5MgF 2 —GeO 2 ; Mn +4 (MFG); Y 3 Al 5 O 12 ; Ce (YAG:Ce 3+ ); (Tb, Y, Lu, La, Gd) 3 (Al, Ga) 5 O 12 :Ce 3+ (TAG:Ce); (Ca, Sr) 8 (Mg,Zn)(SiO 4 ) 4 Cl 2 :Eu 2+ , Mn 2+ (CASI) and combinations thereof.
17. The article of manufacture of claim 14 comprising at least one additional phosphor.
18. The article of manufacture of claim 14 wherein once said first persistent phosphor, said second persistent phosphor and said third non-persistent phosphor have been excited light emitted from said phosphors appears white in an absence of ambient light.
19. The article of manufacture of claim 14 wherein said formula II of said second persistent phosphor is Sr 4-y-z Al 14 O 25 :Eu 2+ y , Dy 3+ z .
20. The article of manufacture of claim 19 wherein said formula I of first persistent phosphor is Ca 1-y-z Al 2 O 4 :Eu 2+ y , Nd 3+ z .
21. The article of manufacture of claim 20 wherein said third phosphor is selected from the group consisting of 3.5MgO-0.5MgF 2 —GeO 2 ; Mn +4 (MFG); Y 3 Al 5 O 12 ; Ce (YAG:Ce 3+ ); (Tb, Y, Lu, La, Gd) 3 (Al, Ga) 5 O 12 :Ce 3+ (TAG:Ce); (Ca, Sr) 8 (Mg,Zn)(SiO 4 ) 4 Cl 2 :Eu 2+ , Mn 2+ (CASI) and combinations thereof.
22. The article of manufacture of claim 14 wherein said third phosphor is selected from the group consisting of a yellow emitter, a yellow-orange emitter, an orange-red emitter, a red emitter and combinations thereof.
23. The article of manufacture of claim 14 comprising three of said layers, wherein said first persistent phosphor, said second persistent phosphor and said third non-persistent phosphor each are present in a different one of said layers.