Microcrystalline cellulose compositions
View Patent ↗Ultra-fine microcrystalline cellulose compositions are disclosed which comprise co-attrited microcrystalline cellulose and a hydrocolloid. The compositions have a mean particle size of less than 10 microns. The compositions are prepared by subjecting a high solids mixture of microcrystalline cellulose and a hydrocolloid to high shear forces in the presence of an anti slip agent preferably an aqueous solution of an inorganic salt. The compositions are especially useful in food, pharmaceutical and cosmetic and industrial applications.
1. A coattrited composition consisting essentially of:
(a) microcrystalline cellulose, and
(b) a hydrocolloid,
wherein (i) the composition has a mean particle size of more than 4.27 microns and less than about 10 microns; (ii) at least about 30% of the particles have a particle size less than about 3.5 microns, and (iii) said composition consists essentially of at least 70% by weight of said microcrystalline cellulose or the ratio of said microcrystalline cellulose to said hydrocolloid is equal to from 50/50 to 90/10, respectively.
2. A composition as claimed in claim 1 wherein the amount of hydrocolloid is equal to from 15% to 30% by weight based on the total weight of hydrocolloid and microcrystalline cellulose.
3. The composition of claim 1 , wherein said microcrystalline cellulose is present in an amount of at least 70% by weight of said composition.
4. The composition of claim 1 , wherein said ratio of said microcrystalline cellulose to said hydrocolloid is equal to from 50/50 to 90/10, respectively.
5. The composition of claim 1 , wherein said composition consists of said microcrystalline cellulose and hydrocolloid.
6. The composition of claim 5 , wherein said hydrocolloid consists of cellulose gum.
7. The composition of claim 1 , wherein said composition has an initial viscosity of 2,000 cps and a set up viscosity of 12,900 cps after 24 hours when both are measured in a 2.6% water dispersion.