Composition, energy storage device, and related processes
View Patent ↗A positive electrode composition is provided. The composition includes at least one electroactive metal, such as titanium, vanadium, niobium, molybdenum, nickel, cobalt, chromium, manganese, silver, antimony, cadmium, tin, lead, and zinc. The composition further includes iron, at least one first alkali metal halide; and an electrolyte salt. The electrolyte salt can be based on a reaction product of a second alkali metal halide and an aluminum halide, and has a melting point of less than about 300 degrees Celsius. An article, an energy storage device, and an uninterruptable power supply device that includes the positive electrode composition are also described; as is a method of forming the energy storage device.
1. A positive electrode composition comprising:
at least one electroactive metal selected from the group consisting of titanium, vanadium, niobium, molybdenum, nickel, cobalt, chromium, manganese, silver, antimony, cadmium, tin, lead, and zinc; wherein the electroactive metal is present in an amount in a range from about 10 volume percent to about 20 volume percent, based on the volume of the positive electrode composition;
iron present in an amount in a range from about 0.5 volume percent to about 1.4 volume percent, based on the volume of the positive electrode composition;
a first alkali metal halide;
an electrolyte salt comprising a reaction product of a second alkali metal halide and an aluminum halide, wherein the electrolyte salt has a melting point of less than about 300 degrees Celsius; and
sulfur present in an amount in a range from about 0.1 weight percent to about 3 weight percent based on the total weight of the positive electrode composition.
2. The positive electrode composition of claim 1 , wherein the aluminum halide is aluminum chloride.
3. The positive electrode composition according to claim 1 , wherein the at least one electroactive metal is nickel.
4. The positive electrode composition according to claim 1 , wherein the first and second alkali metals comprise, independently, sodium, potassium, or lithium.
5. The positive electrode composition according to claim 1 , wherein the first and second halides comprise, independently, at least one halogen selected from chlorine, bromine, and fluorine.
6. The positive electrode composition according to claim 1 , wherein the electroactive metal is present in a range of from about 11 volume percent to about 19 volume percent, based on the volume of the positive electrode composition.
7. The positive electrode composition according to claim 1 , wherein sulfur is present in the form of molecular sulfur, or a sulfur-containing compound.
8. The positive electrode composition according to claim 1 , further comprising additional aluminum, in a form other than the aluminum halide.
9. The positive electrode composition according to claim 8 , wherein the additional aluminum is present in a range of from about 0.2 volume percent to about 0.5 volume percent, based on the volume of the positive electrode composition.
10. An article, comprising:
a positive electrode, which itself comprises:
at least one electroactive metal selected from the group consisting of titanium, vanadium, niobium, molybdenum, nickel, cobalt, chromium, manganese, silver, antimony, cadmium, tin, lead, and zinc; wherein the electroactive metal is present in an amount in a range from about 10 volume percent to about 20 volume percent based on the volume of the positive electrode composition;
iron present in an amount in a range from about about 0.5 volume percent to about 1.4 volume percent, based on the volume of the positive electrode composition;
a first alkali metal halide;
an electrolyte salt comprising a reaction product of a second alkali metal halide and an aluminum halide, wherein the electrolyte salt has a melting point of less than about 300 degrees Celsius; and
sulfur present in an amount in a range from about 0.1 weight percent to about 3 weight percent based on the total weight of the positive electrode composition.
11. The article according to claim 10 , wherein the article is an energy storage device.
12. The article according to claim 10 , in the form of an uninterruptable power supply device.
13. An uninterruptable power supply device comprising:
a positive electrode which itself comprises
at least one electroactive metal selected from the group consisting of titanium, vanadium, niobium, molybdenum, nickel, cobalt, chromium, manganese, silver, antimony, cadmium, tin, lead, and zinc; wherein the electroactive metal is present in an amount in a range from about 10 volume percent to about 20 volume percent, based on the volume of the positive electrode composition;
iron present in an amount in a range from about 0.5 volume percent to about 1.4 volume percent, based on the volume of the positive electrode composition;
a first alkali metal halide;
an electrolyte salt comprising a reaction product of a second alkali metal halide and an aluminum halide, wherein the electrolyte salt has a melting point of less than about 300 degrees Celsius; and
sulfur present in an amount in a range from about 0.1 weight percent to about 3 weight percent based on the total weight of the positive electrode composition.
14. A positive electrode composition comprising:
nickel in an amount in a range from about 10 volume percent to about 20 volume percent, based on the volume of the positive electrode composition;
iron present in an amount in a range from about 0.5 volume percent to about 1.4 volume percent, based on the volume of the positive electrode composition;
a first alkali metal halide selected from sodium chloride, sodium fluoride, sodium iodide, and a combination thereof;
an electrolyte salt comprising a reaction product of
(a) a second alkali metal halide selected from sodium chloride, sodium fluoride, sodium iodide, and a combination thereof; and
(b) an aluminum halide,
wherein the electrolyte salt has a melting point of less than about 300 degrees Celsius; and
sulfur present in an amount in a range from about 0.1 weight percent to about 3 weight percent based on the total weight of the positive electrode composition.