CONTOURABLE CORE FABRIC AND METHOD OF MAKING SAME
A method includes providing an open weave fiber glass scrim, and printing a discontinuous pattern of an ethylene vinyl acetate (EVA) hot melt adhesive on a major surface of the open weave fiber glass scrim, the adhesive having sufficient viscosity at an application temperature used during the printing step to avoid wicking through the scrim.
1 . A method comprising:
providing an open weave fiber glass scrim;
printing a discontinuous pattern of an ethylene vinyl acetate (EVA) hot melt adhesive on a major surface of the open weave fiber glass scrim, the adhesive having sufficient viscosity at an application temperature used during the printing step to avoid wicking through the scrim.
2 . The method of claim 1 , wherein the adhesive has a softening point in a range from 60° C. to 140° C.
3 . The method of claim 1 , wherein the adhesive has a softening point in a range from 60° C. to 90° C.
4 . The method of claim 1 , wherein the adhesive has a viscosity at the application temperature in a range from 1000 to 150,000 centipoises at 191° C.
5 . The method of claim 1 , wherein the viscosity at the application temperature is in a range from 10,000 to 60,000 centipoises at 191° C.
6 . The method of claim 1 , wherein the providing step includes forming the scrim using a dry warped beam.
7 . The method of claim 1 , wherein the scrim is a greige scrim.
8 . The method of claim 1 , wherein the printing step is a gravure process.
9 . The method of claim 8 , wherein the gravure process includes using a gravure roll having from 10 to 55 parallel engraved lines per inch (4 to 22 parallel lines per centimeter) in at least one direction.
10 . The method of claim 9 , wherein the lines form a diamond pattern, and the lines are oriented at an angle from 30 degrees to 60 degrees from a machine direction of the scrim.
11 . The method of claim 8 , wherein the gravure process includes using a gravure roll and the method further comprises directing hot air using a hot air knife directed at a gap between the gravure roll and the scrim.
12 . The method of claim 8 , wherein the gravure process includes using a gravure roll and the method further comprises using a hot wire to cut one or more strings of adhesive that form during the gravure process.
13 . The method of claim 1 , wherein the printing step includes applying the adhesive with an average area density of 5 grams/meter 2 to 28 grams/meter 2 .
14 . The method of claim 13 , wherein the printing step includes applying the adhesive with an average area density of 20 grams/meter 2 to 28 grams/meter 2 .
15 . A product, comprising:
an open weave fiber glass scrim; and
a discontinuous pattern of EVA hot melt adhesive applied on one side of the open weave fiber glass scrim without bleeding through the scrim.
16 . The product of claim 15 , wherein:
the adhesive has a softening point in a range from 60° C. to 90° C.; and
the viscosity at the application temperature is in a range from 10,000 to 60,000 centipoises.
17 . The product of claim 16 , wherein:
the scrim is a greige scrim; and
the adhesive has an average area density of 20 grams/meter 2 to 28 grams/meter 2 .
18 . The product of claim 15 , wherein:
the discontinuous pattern of adhesive includes adhesive with an average area density of 20 grams/meter 2 to 27 grams/meter 2 . arranged in line segments lying along lines spaced at from 25 to 55 parallel lines per inch (10 to 22 parallel lines per centimeter) in at least one direction.
19 . A method of using the product of claim 15 , comprising:
laminating the scrim to at least one panel from the group consisting of expanded polymer foam and wood, with the adhesive joining the scrim to the panel; and
slitting the foam or wood in two directions without slitting the scrim to form a contourable core material having a plurality of blocks attached to the scrim.
20 . The method of claim 18 , further comprising:
laminating facing sheets on both major faces of the contourable core material.