Coating compositions having improved early hardness
View Patent ↗A fast hardening clear coating composition for repairing a clear coat/color coat finish or a pigmented mono-coat of a vehicle comprising a film forming binder and an organic liquid carrier, where the binder contains a hydroxyl polymer component comprising (A) hydroxyl-containing acrylic polymer, (B) at least one hydroxyl-terminated component selected from the group consisting of (1) an organic diol having the formula where R 1 and R 2 are individually selected from the group of hydrogen and an alkyl group having 1, 3-5 carbon atoms and (2) a hydroxyl terminated reaction product of trimethylol propane and a lactone; (C) an organic polyisocyanate crosslinking component, at least portion of which comprises a trimer of isophorone diisocyanate or hexamethylene diisocyanate and the composition further contains, a curing catalyst, of a dialkyl tin aliphatic carboxylate, a tertiary aliphatic mono or diamine, an aliphatic carboxylic acid, and optionally, a zinc or calcium organic acid salt in an effective amount such that the coating composition on curing at ambient temperatures is in a water spot free and sufficiently hard state for sanding or buffing within about 2 hours after application or on cool down when baked under normal conditions.
1. A process for repairing a clear coat of a clear coat/color coat coating composition which comprises applying a layer of a clear coating composition to the clear coat and curing the layer of the applied clear coating composition,
wherein, said clear coating composition contains a film forming binder and a volatile organic liquid carrier for the binder, wherein the film forming binder contains:
(A) a hydroxyl polymer component comprising at least one hydroxyl-containing acrylic polymer;
(B) at least one hydroxyl-terminated component selected from the group consisting of (1) an organic diol having the formula
where R 1 and R 2 are individually selected from the group consisting of hydrogen and an alkyl group having 1, 3-5 carbon atoms and (2) a hydroxyl terminated reaction product of trimethylol propane and a lactone; and
(C) an organic polyisocyanate component, at least a portion of which comprises a trimer selected from the group consisting of a trimer of isophorone diisocyanate and a trimer of hexamethylene diisocyanate and any mixtures thereof, wherein the organic polyisocyanate component further comprises at least one of an asymmetric hexamethylene diisocyanate trimer, a biuret of hexamethylene diisocyanate, a biuret of isophorone diisocyanate and any mixtures thereof;
wherein the ratio of equivalents of isocyanate per equivalent of hydroxyl groups in the binder is in the range of about 0.7/1 to 2.0/1; and
wherein the clear coating composition further contains
(D) a catalyst system for the binder comprising
(i) at least one organotin compound,
(ii) at least one tertiary amine,
(iii) at least one organic carboxylic acid; and
(iv) optionally, at least one organic acid salt selected from the group consisting of zinc organic acid salts and calcium organic salts;
wherein the clear coating composition cures at ambient temperatures to a water spot free state within 2 hours after application;
wherein the hydroxyl containing acrylic polymer comprises 5 to 50% by weight, based on the weight of the acrylic polymer, of a hydroxyl acrylic polymer having a weight average molecular weight of above 10,000 to 20,000, 20-60% by weight, based on the weight of the acrylic polymer, of a hydroxyl acrylic polymer having a weight average molecular weight of above 7,000 and up to 10,000 and 20-70% by weight by weight, based on the weight of the acrylic polymer, of a hydroxyl acrylic polymer having a weight average molecular weight of 2,000 up to 7,000.
2. A process for repairing a pigmented mono-coat finish which comprises applying a layer of a pigmented coating composition to the mono coat finish and curing the layer of the applied pigmented coating composition,
wherein, said pigmented coating composition contains a film forming binder, one or more pigments and a volatile organic liquid carrier for the binder, wherein the film forming binder contains:
(A) a hydroxyl polymer component comprising at least one hydroxyl-containing acrylic polymer;
(B) at least one hydroxyl-terminated component selected from the group consisting of (1) an organic diol having the formula
where R 1 and R 2 are individually selected from the group consisting of hydrogen and an alkyl group having 1, 3-5 carbon atoms and (2) a hydroxyl terminated reaction product of trimethylol propane and a lactone; and
(C) an organic polyisocyanate component, at least a portion of which comprises a trimer selected from the group consisting of a trimer of isophorone diisocyanate and a trimer of hexamethylene diisocyanate and any mixtures thereof, wherein the organic polyisocyanate component further comprises at least one of an asymmetric hexamethylene diisocyanate trimer, a biuret of hexamethylene diisocyanate, a biuret of isophorone diisocyanate and any mixtures thereof;
wherein the ratio of equivalents of isocyanate per equivalent of hydroxyl groups in the binder is in the range of about 0.7/1 to 2.0/1;
and
wherein the pigmented coating composition further contains
(D) a catalyst system for the binder comprising
(i) at least one organotin compound,
(ii) at least one tertiary amine,
(iii) at least one organic carboxylic acid; and
(iv) optionally, at least one organic acid salt selected from the group consisting of zinc organic acid salts and calcium organic salts;
wherein the one or more pigments are present in the pigmented coating composition in a pigment to binder weight ratio in a range of from about 0.1:100 to 300:100;
wherein the pigmented coating composition cures at ambient temperatures to a water spot free state within 2 hours after application;
wherein the hydroxyl containing acrylic polymer comprises 5 to 50% by weight, based on the weight of the acrylic polymer, of a hydroxyl acrylic polymer having a weight average molecular weight of above 10,000 to 20,000, 20-60% by weight, based on the weight of the acrylic polymer, of a hydroxyl acrylic polymer having a weight average molecular weight of above 7,000 and up to 10,000 and 20-70% by weight by weight, based on the weight of the acrylic polymer, of a hydroxyl acrylic polymer having a weight average molecular weight of 2,000 up to 7,000.