Ink-jet print head having improved adhesion with time, its process of manufacturing and its use in combination with a water-based ink containing acidic species

1. A process for manufacturing an ink-jet print head for an ink-jet printer comprising a photopolymer barrier defining ink passage ways and ejection chambers formed on a substrate, said process comprising the steps of:

providing a substrate,

applying, on said surface of said substrate, an adhesive first layer of a photopolymer barrier, said first layer being made of a partially polymerized cationically polymerizable material,

applying a second layer above said first layer, said second layer being made of photopolymerizable material,

providing ink passage ways and ejection chambers, and

contacting said ink-jet print head with a water-based ink containing acidic species with a pH value between 3 and 5 so as to further polymerize said partially polymerized adhesive first layer of said photopolymer barrier, thus improving the photopolymer barrier adhesion on said surface of said substrate with time.

2. The process for manufacturing an ink-jet print head according to claim 1 , including forming on the surface of the substrate a plurality of ink ejection energy generating elements.

3. The process for manufacturing an ink-jet print head according to claim 1 , wherein said cationically polymerizable material partially polymerized forming said adhesive first layer is selected from the group consisting of epoxy resins.

4. The process for manufacturing an ink-jet print head according to claim 1 , wherein said water-based ink containing acidic species is obtained by adding to water an acid or a substance able to release an acid.

5. The process for manufacturing an ink-jet print head according to claim 4 , wherein said acid or said substance able to release an acid is selected from the group consisting of non-corrosive inorganic acids, organic acids, hydrolysable salts and hydrolysable esters.

6. The process for manufacturing an ink-jet print head according to claim 5 , wherein said acid or said substance able to release an acid is selected among hydrolysable esters.

7. The process for manufacturing an ink-jet print head according to claim 6 , wherein said hydrolysable esters are hydrolysable acrylic esters.

8. The process for manufacturing an ink-jet print head according to claim 7 , wherein said hydrolysable acrylic esters are polyethylene glycol (PEG) diacrylates.

9. The process for manufacturing an ink-jet print head according to claim 8 , wherein said hydrolysable acrylic esters are PEG diacrylates with molecular weight comprised between 200 amu and 1,000 amu.

10. The process for manufacturing an ink-jet print head according to claim 4 , wherein said water-based ink containing acidic species reaches a pH value comprised between 3 and 5 over time.

11. A process of polymerizing at least a part of an ink-jet print head for an ink-jet printer in a water-based ink containing acidic species with a pH value between 3 and 5, said ink-jet print head comprising at least a substrate and a photopolymer barrier applied onto said substrate, said photopolymer barrier comprising an adhesive first layer being made of a partially polymerized cationically polymerizable material and a second layer being made of a photopolymerizable material applied above said first layer, said process comprising:

contacting the adhesive first layer with the water-based ink containing acidic species having a pH value between 3 and 5, whereby the adhesive first layer is further polymerized, so as to improve a photopolymer barrier adhesion on said surface of said substrate over time.