Process for producing a roll for supporting and conveying hot material, process for repairing a worn roll
View Patent ↗A roll ( 1 ) for supporting and conveying hot material, including a roll element that has a roll jacket ( 2 ) made of a basic material and a wear coat which is applied to the basic material by means of a surface welding process ( 4 ) using a welding additive which surrounds the surface of the roll jacket. In order to increase the service life of the wear coat, improve the resistance to wear, and reduce the cost for producing the welded-on surface. The basic material of the roll jacket ( 2 ) is steel and contains up to 0.45 percent of C. The welded-on surface ( 4 ) is designed as a single-layer weld, and the wear coat contains 12.5 to 14.0 percent of Cr at least in an external zone that surrounds the surface of the roll jacket. Also disclosed are a method for producing the roll ( 1 ), a method for repairing a used roll ( 1 ), a welding additive and a welding rod for producing the welded-on surface.
1. A process for producing a roll for supporting and conveying hot material on a roller table or in a continuous casting machine, the roll having a roll body, which comprises:
a roll shell of a base material and a roll shell surface; and
a wearing layer, which has been applied to the base material by build-up welding using a weld filler, wherein the base material of the roll shell is steel,
the process comprising the following steps:
forming the roll shell or roll body from a base material as a rotating part,
applying a build-up weld layer to the base material by single-layer build-up welding with a minimum thickness of the build-up weld layer of 3.5 mm,
turning back the build-up weld layer on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 1.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness, and
wherein the single layer build-up welding is carried out by open arc build-up welding process.
2. The process as claimed in claim 1 , wherein the build-up welding on the base material produces a minimum thickness of the build-up weld layer of 4.0 mm or more.
3. The process as claimed in claim 1 , wherein the build-up weld layer is turned back on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 2.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness.
4. The process as claimed in claim 1 , further comprising the base material of the roll shell comprises steel containing up to 0.45% C.
5. The process as claimed in claim 1 , further comprising the weld filler having the following composition for the build-up welding:
18.5 to 19.0% Cr
0.15 to 0.20% Nb
4.5% Ni
1.0% Mo
0.12% N
0.7% Si
1.2% Mn
0.03% C
max. 0.025% S
max. 0.025% P
remainder Fe and manufacturing-related impurities,
where the spread of the individual alloy components is +/−5%.
6. The process as claimed in claim 1 , further comprising the base material of the roll shell comprises steel containing 0.2 to 0.45% C.
7. The process as claimed in claim 1 , wherein the process is carried out to produce continuously cast steel strands.
8. The process as claimed in claim 1 , further comprising the build-up welding comprises an iron-based weld filler having a Cr content of 16.5 to 19.0%.
9. The process as claimed in claim 8 , wherein the weld filler additionally contains 0.15 to 0.20% Nb used for the build-up welding.
10. The process as claimed in claim 8 , further comprising a weld filler having the following composition for the build-up welding:
16.5 to 19.0% Cr
0.15 to 0.20% Nb
4.0 to 4.5% Ni
1.0% Mo
0.12% N
0.7% Si
1.2% Mn
0.03% C
max. 0.025% S
max. 0.025% P
remainder Fe and manufacturing-related impurities,
where the spread of the individual alloy components is +/−5%.
11. The process as claimed in claim 9 , further comprising a weld filler having the following composition for the build-up welding:
16.5 to 17.0% Cr
0.15 to 0.20% Nb
4.0% Ni
1.0% Mo
0.12% N
0.7% Si
1.2% Mn
0.03% C
max. 0.025% S
max. 0.025% P
remainder Fe and manufacturing-related impurities,
where the spread of the individual alloy components is +/−5%.
12. A process for producing a roll for supporting and conveying hot material on a roller table or in a continuous casting machine, the roll having a roll body, which comprises:
a roll shell of a base material and a roll shell surface; and
a wearing layer, which has been applied to the base material by build-up welding using a weld filler, wherein the base material of the roll shell is steel,
the process comprising the following steps:
forming the roll shell or roll body from a base material as a rotating part,
applying a build-up weld layer to the base material by single-layer build-up welding with a minimum thickness of the build-up weld layer of 3.5 mm,
turning back the build-up weld layer on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 1.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness,
wherein a weld filler having the following composition for the build-up welding:
16.5 to 19.0% Cr
0.15 to 0.20% Nb
4.0 to 4.5% Ni
1.0% Mo
0.12% N
0.7% Si
1.2% Mn
0.03% C
max. 0.025% S
max. 0.025% P
remainder Fe and manufacturing-related impurities,
where the spread of the individual alloy components is +/−5%,
wherein the build-up welding comprises an iron-based weld filler having a Cr content of 16.5 to 19.0% and
wherein the weld filler additionally contains 0.15 to 0.20% Nb used for the build-up welding.
13. The process as claimed in claim 12 , wherein the build-up welding on the base material produces a minimum thickness of the build-up weld layer of 4.0 mm or more.
14. The process as claimed in claim 12 , wherein the build-up weld layer is turned back on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 2.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness.
15. The process as claimed in claim 12 , further comprising the base material of the roll shell comprises steel containing up to 0.45% C.
16. The process as claimed in claim 12 , further comprising the base material of the roll shell comprises steel containing 0.2 to 0.45% C.
17. The process as claimed in claim 12 , wherein the process is carried out to produce continuously cast steel strands.
18. A process for producing a roll for supporting and conveying hot material on a roller table or in a continuous casting machine, the roll having a roll body, which comprises:
a roll shell of a base material and a roll shell surface; and
a wearing layer, which has been applied to the base material by build-up welding using a weld filler, wherein the base material of the roll shell is steel,
the process comprising the following steps:
forming the roll shell or roll body from a base material as a rotating part,
applying a build-up weld layer to the base material by single-layer build-up welding with a minimum thickness of the build-up weld layer of 3.5 mm,
turning back the build-up weld layer on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 1.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness,
wherein the weld filler has the following composition for the build-up welding:
16.5 to 17.0% Cr
0.15 to 0.20% Nb
4.0% Ni
1.0% Mo
0.12% N
0.7% Si
1.2% Mn
0.03% C
max. 0.025% S
max. 0.025% P
remainder Fe and manufacturing-related impurities,
where the spread of the individual alloy components is +/−5% and
wherein the build-up welding comprises an iron-based weld filler having a Cr content of 16.5 to 19.0% and
wherein the weld filler additionally contains 0.15 to 0.20% Nb used for the build-up welding.
19. The process as claimed in claim 18 , wherein the build-up welding on the base material produces a minimum thickness of the build-up weld layer of 4.0 mm or more.
20. The process as claimed in claim 18 , wherein the build-up weld layer is turned back on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 2.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness.
21. The process as claimed in claim 18 , further comprising the base material of the roll shell comprises steel containing up to 0.45% C.
22. The process as claimed in claim 18 , further comprising the base material of the roll shell comprises steel containing 0.2 to 0.45% C.
23. The process as claimed in claim 18 , wherein the process is carried out to produce continuously cast steel strands.
24. A process for producing a roll for supporting and conveying hot material on a roller table or in a continuous casting machine, the roll having a roll body, which comprises:
a roll shell of a base material and a roll shell surface; and
a wearing layer, which has been applied to the base material by build-up welding using a weld filler, wherein the base material of the roll shell is steel,
the process comprising the following steps:
forming the roll shell or roll body from a base material as a rotating part,
applying a build-up weld layer to the base material by single-layer build-up welding with a minimum thickness of the build-up weld layer of 3.5 mm,
turning back the build-up weld layer on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 1.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness,
wherein the weld filler has the following composition for the build-up welding:
18.5 to 19.0% Cr
0.15 to 0.20% Nb
4.5% Ni
1.0% Mo
0.12% N
0.7% Si
1.2% Mn
0.03% C
max. 0.025% S
max. 0.025% P
remainder Fe and manufacturing-related impurities,
where the spread of the individual alloy components is +/−5%.
25. The process as claimed in claim 24 , wherein the build-up welding on the base material produces a minimum thickness of the build-up weld layer of 4.0 mm or more.
26. The process as claimed in claim 24 , wherein the build-up weld layer is turned back on a closed, unifacial roll shell surface while maintaining a minimum thickness of the wearing layer of 2.5 mm or more, wherein the wearing layer has an identical chemical composition through the minimum thickness.
27. The process as claimed in claim 24 , further comprising the base material of the roll shell comprises steel containing up to 0.45% C.
28. The process as claimed in claim 24 , further comprising the base material of the roll shell comprises steel containing 0.2 to 0.45% C.
29. The process as claimed in claim 24 , wherein the process is carried out to produce continuously cast steel strands.
30. The process as claimed in claim 24 , further comprising the build-up welding comprises an iron-based weld filler having a Cr content of 16.5 to 19.0%.
31. The process as claimed in claim 30 , wherein the weld filler additionally contains 0.15 to 0.20% Nb used for the build-up welding.