Positive electrode containing lithium nickel composite oxide for non-aqueous electrolyte secondary battery, non-aqueous electrolyte secondary battery using the same, and method for producing the same
View Patent ↗A method for producing a positive electrode for non-aqueous electrolyte secondary battery of the present invention includes the steps of: (1) producing a positive electrode precursor by applying a positive electrode slurry including a positive electrode active material comprising a lithium-containing composite oxide including nickel, a binder, and a conductive agent on a positive electrode core material, the positive electrode active material including secondary particles having an average particle diameter of 8 μm or more, and then drying the positive electrode slurry to form a positive electrode material mixture layer; and (2) rolling while heating the positive electrode precursor to produce a positive electrode in which 3.5 g or more of the positive electrode active material is included per 1 cm 3 of the positive electrode material mixture layer, and the positive electrode active material includes secondary particles having an average particle diameter of 5 μm or more.
1. A positive electrode for non-aqueous electrolyte secondary battery comprising: a positive electrode core material; and a positive electrode material mixture layer formed on a surface of said positive electrode core material,
wherein said positive electrode material mixture layer includes a positive electrode active material, a binder, and a conductive agent,
said positive electrode active material includes a lithium-containing composite oxide including nickel,
said lithium-containing composite oxide has a hexagonal crystal structure, and a content of said nickel accounts for 60 to 90% by mol of all metallic elements other than lithium,
said lithium-containing composite oxide includes secondary particles having an average particle diameter of 5 μm or more, and
3.5 g or more of said positive electrode active material is included per 1 cm 3 of said positive electrode material mixture layer.
2. The positive electrode for non-aqueous electrolyte secondary battery in accordance with claim 1 ,
wherein said lithium-containing composite oxide is represented by the general formula:
Li a Ni 1-x M x O 2+b ,
where M is at least one selected from the group consisting of Co, Fe, Cu, Mn, Al, Mg, Ti, Zr, Ce, and Y; 0.1≦x≦0.4; 0.97≦a≦1.05; and −0.1≦b≦0.1.
3. A non-aqueous electrolyte secondary battery comprising: the positive electrode in accordance with claim 1 ; a negative electrode including a negative electrode active material; a separator interposed between said positive electrode and said negative electrode; and a non-aqueous electrolyte.