Rubber composition for tire including a novel anti-oxidant system
View Patent ↗Rubber composition, especially for a tire, based on at least one diene elastomer, a reinforcing filler, a crosslinking system and an antioxidant system, wherein said antioxidant system comprises at least two antioxidants “A” and “B”: A. an N-alkyl-N′-phenyl-para-phenylenediamine corresponding to the formula (I): B. a 4,4′,4″-tris(alkylamino)triphenylamine corresponding to the formula (II): in which formulae, R 1 , R 2 , R 3 and R 4 , which are identical or different, each represent a linear or branched alkyl group having from 1 to 12 carbon atoms or a cycloalkyl group having from 5 to 8 carbon atoms, the A/B weight ratio being between 0.1 and 5.0.
1. A rubber composition based on at least one diene elastomer, a reinforcing filler, a crosslinking system and an antioxidant system, wherein said antioxidant system comprises at least two antioxidants “A” and “B”:
A. an N-alkyl-N′-phenyl-para-phenylenediamine corresponding to the formula (I):
B. a 4,4′,4″-tris(1,4-dimethylpentylamino)triphenylamine corresponding to the formula (IV-b):
in which formulae, R 1 represents a linear or branched alkyl group having from 1 to 12 carbon atoms or a cycloalkyl group having from 5 to 8 carbon atoms, the A/B weight ratio being between 1/10 and 5/1.
2. The composition according to claim 1 , wherein antioxidant A is N-isopropyl-N′-phenyl-para-phenylenediamine corresponding to the formula (III-a):
3. The composition according to claim 1 , wherein antioxidant A is N-1,3-dimethylbutyl-N′-phenyl-para phenylenediamine corresponding to the formula (III-b):
4. The composition according to 1 , wherein the content of each antioxidant A and B is between 0.5 and 5 phr, preferably between 0.5 and 3 phr.
5. The composition according to 1 , wherein the AB weight ratio is between 1/7 and 4/1.
6. The composition according to 1 , wherein the diene elastomer is chosen from the group formed by polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, isoprene copolymers and blends of these elastomers.
7. The composition according to claim 6 , wherein the diene elastomer is an isoprene elastomer.
8. The composition according to claim 7 , wherein the isoprene elastomer is chosen from the group composed of natural rubber, synthetic cis-1,4-polyisoprenes, isoprene copolymers and blends of these elastomers.
9. The composition according to claim 8 , wherein the isoprene elastomer is natural rubber.
10. A tire comprising a rubber composition according to claim 1 .
11. The tire according to claim 10 , said tire being a heavy vehicle tire.
12. The tire according to claim 10 , the rubber composition being in the belt of said tire.
13. A process for preparing a rubber composition based on at least one diene elastomer, a reinforcing filler, a crosslinking system and an antioxidant system, said process comprising the steps of:
a. incorporating into a diene elastomer, in a mixer:
(i) a reinforcing filler; and
(ii) an antioxidant system,
by thermomechanically kneading the entire mixture, in one or more stages, until a maximum temperature between 110° C. and 190° C. is reached;
b. cooling the entire mixture to a temperature below 100° C.;
c. then incorporating a crosslinking system; and
d. kneading the entire mixture up to a maximum temperature below 110° C.,
wherein said antioxidant system comprises at least two antioxidants “A” and “B”:
A an N-alkyl-N′-phenyl-para-phenylenediamine corresponding to the formula (I):
B. a 4,4′,4″-tris(1,4-dimethylpentylamino)triphenylamine corresponding to the formula (IV-b):
in which formulae, R 1 represents a linear or branched alkyl group having from 1 to 12 carbon atoms or a cycloalkyl group having from 5 to 8 carbon atoms, the A/B weight ratio being between 1/10 and 5/1.