IP Library › Granted Patent US 9,034,989

Granted Patent B2

US 9,034,989 · App. 13/001,019 · Granted May 19, 2015

Branched PHA compositions, methods for their production, and use in applications

View Patent ↗

Loading inventors, assignments & file history…

Monitor This Case

Get email alerts when status or documents change.

Order Certified Copies

Most orders are placed with the USPTO same day — all within 24 business hours.

Order via The Patent Place →

Pre-filled with this patent's details

Quick Facts

Patent No.: US 9,034,989
App. No.: 13/001,019
Granted: May 19, 2015
Kind: B2

External Links

USPTO Patent Center↗ Full Patent PDF↗

Abstract

Branched PHA compositions, and related methods and articles are disclosed.

Claims (46)

1. A method of branching a starting polyhydroxyalkanoate polymer (PHA), comprising reacting the starting PHA with a branching agent in the presence of at least two cross-linking agents, thereby forming a branched PHA, wherein the branching agent is peroxide, azo-nitrile, perester or peroxycarbonate, and wherein the cross-linking agents are

an epoxy functional compound containing two or more epoxide groups and

a compound comprising at least two double bonds.

2. The method claim 1 , wherein the branching agent is selected from: dicumyl peroxide, t-amyl-2-ethylhexyl peroxycarbonate, 1,1-bis(t-butylperoxy)-3,3,5-trimethylcyclohexane, 2,5-dimethyl-2,5-di(t-butylperoxy) hexane, 2,5-bis(t-butylperoxy)-2,5-dimethylhexane, 2,5-dimethyl-di(t-butylperoxy)hexyne-3, di-t-butyl peroxide, benzoyl peroxide, di-t-amyl peroxide, t-butyl cumyl peroxide, n-butyl-4,4-bis(t-butylperoxy)valerate, 1,1-di(t-butylperoxy)-3,3,5-trimethyl-cyclohexane, 1,1-di(t-butylperoxy)cyclohexane, 1,1-di(t-amylperoxy)-cyclohexane, 2,2-di(t-butylperoxy)butane, ethyl-3,3-di(t-butylperoxy)butyrate, 2,2-di(t-amylperoxy)propane, ethyl-3,3-di(t-amylperoxy)butyrate, t-butylperoxy-acetate, t-amylperoxyacetate, t-butylperoxybenzoate, t-amylperoxybenzoate, and di-t-butyldiperoxyphthalate.

3. The method of claim 1 , wherein the concentration of branching agent is between 0.001 to 0.5% by weight of the PHA.

4. The method of claim 1 , wherein the melt strength (elasticity) (G′) of the branched PHA is greater than the melt strength of the starting PHA.

5. The method of claim 4 , wherein the melt strength of the branched PHA is at least twice to about 20 times that of the starting PHA as measured at 0.25 rad/sec at 160° C.

6. A method of branching a starting polyhydroxyalkanoate polymer PHA comprising reacting the starting PHA with a branching agent and a cross-linking agent, thereby forming a branched PHA, provided that the branching agent is optionally omitted when the cross-linking agent is an epoxy functional compound, wherein the starting PHA is thermolysed to reduce its molecular weight between 25-75% before reacting with the branching agent, wherein the starting PHA is thermolysed in the presence of the cross-linking agent.

7. The method of claim 1 , wherein one cross-linking agent is an epoxy-functional styrene-acrylic polymer, an epoxy-functional acrylic copolymer, an epoxy-functional polyolefin copolymer, an oligomer comprising a glycidyl group with an epoxy functional side chain, an epoxy-functional poly(ethylene-glycidyl methacrylate-co-methacrylate), an epoxidized oil, diallyl phthalate, pentaerythritol tetraacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, dipentaerythritol pentaacrylate, diethylene glycol dimethacrylate, or bis(2-methacryloxyethyl)phosphate.

8. The method of claim 1 , wherein, the polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate), a poly(3-hydroxybutyrate-co-3-hydroxyvalerate), a poly(3-hydroxybutyrate-co-5-hydroxyvalerate), or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate);

a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content, a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with 5% to 22% 3-hydroxyvalerate content, a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with 5% to 15% 5-hydroxyvalerate content, or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with 3% to 15% 3-hydroxyhexanoate content;

a polymer blend of a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate);

a polymer blend of a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content;

a polymer blend of a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended to with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); wherein the weight of polymer a) is 20% to 60% of the combined weight of polymer a) and polymer b) and the weight of polymer b) is 40% to 80% of the combined weight of polymer a) and polymer b);

a polymer blend of a) poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate; or a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content;

a polymer blend of a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); or a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); wherein the weight of polymer a) is 20% to 60% of the combined weight of polymer a) and polymer b) and the weight of polymer b is 40% to 80% of the combined weight of polymer a) and polymer b).

9. A method of branching a starting polyhydroxyalkanoate polymer PHA comprising reacting the starting PHA with a branching agent and a cross-linking agent, thereby forming a branched PHA, provided that the branching agent is optionally omitted when the cross-linking agent is an epoxy functional compound wherein, the starting polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate), a poly(3-hydroxybutyrate-co-3-hydroxyvalerate), a poly(3-hydroxybutyrate-co-5-hydroxyvalerate), or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate);

10. A branched polyhydroxyalkanoate polymer made by the method of claim 1 , comprising a plurality of PHA chains connected through a cross linking agent.

11. The branched polymer of claim 10 , comprising a plurality of PHAs, connected at an end to another PHA through a functional cross-linking agent.

12. The branched polyhydroxyalkanoate polymer of claim 10 , wherein, the polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate), a poly(3-hydroxybutyrate-co-3-hydroxyvalerate), a poly(3-hydroxybutyrate-co-5-hydroxyvalerate), or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate; a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content, a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with 5% to 22% 3-hydroxyvalerate content, a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with 5% to 15% 5-hydroxyvalerate content, or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with 3% to 15% 3-hydroxyhexanoate content;

13. A branched polyhydroxyalkanoate polymer made by a method of branching a starting polyhydroxyalkanoate polymer (PHA), the method comprising reacting the starting PHA with a branching agent and a cross-linking agent, thereby forming a branched PHA, provided that the branching agent is optionally omitted when the cross-linking agent is an epoxy functional compound; wherein the branched polyhydroxyalkanoate polymer comprises a plurality of PHA chains connected through a cross linking agent; and the polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate), a poly(3-hydroxybutyrate-co-3-hydroxyvalerate), a poly(3-hydroxybutyrate-co-5-hydroxyvalerate), or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate; a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content, a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with 5% to 22% 3-hydroxyvalerate content, a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with 5% to 15% 5-hydroxyvalerate content, or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with 3% to 15% 3-hydroxyhexanoate content;

14. A blown film, comprising the branched PHA polymer of claim 10 .

15. A thermoformed article made by

a) reacting a starting PHA with a branching agent in the presence of a cross-linking agent at a temperature above the decomposition temperature of the branching agent, thereby forming a branched PHA,

b) extruding the branched PHA,

c) thermoforming the branched PHA, thereby forming a thermoformed article, wherein the starting PHA comprises a copolymer blend comprising a poly (3-hydroxybutyrate-co-4-hydroxybutyrate) polymer and the cross-linking agent is diethylene glycol dimethacrylate.

16. A method of branching a starting polyhydroxyalkanoate polymer (PHA), comprising reacting the starting PHA with a branching agent and a cross-linking agent, thereby forming a branched PHA, provided that the branching agent is optionally omitted when the cross-linking agent is an epoxy functional compound, wherein the starting PHA comprises a copolymer blend comprising a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) polymer and the cross-linking agent is diethylene glycol dimethacrylate.

17. The method of claim 1 , wherein the epoxy-functional compound is

an epoxy-functional, styrene-acrylic polymer, an acrylic and/or polyolefin copolymer or oligomer containing glycidyl groups incorporated as side chains, or an epoxidized oil.

18. The method of claim 1 , wherein the cross-linking agent with two or more double bonds is diallyl phthalate, pentaerythritol tetraacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, dipentaerythritol pentaacrylate, diethylene glycol dimethacrylate, bis(2-methacryloxyethyl)phosphate.

Assignments (4)

ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Aug 30, 2017

From: CJ RESEARCH CENTER LLC

To: CJ CHEILJEDANG CORPORATION

Reel/Frame 043723/0517 →

ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jan 3, 2017

From: METABOLIX, INC.

To: CJ RESEARCH CENTER LLC

Reel/Frame 041234/0890 →

ADDRESS CHANGE Recorded May 2, 2016

From: METABOLIX, INC.

To: METABOLIX, INC.

Reel/Frame 038665/0359 →

ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded May 13, 2011

From: PADWA, ALLEN R.; KANN, YELENA; WHITEHOUSE, ROBERT S.; SHEEHAN, KEVIN

To: METABOLIX, INC.

Reel/Frame 026277/0971 →