Phase stable doped zirconia electrolyte compositions with low degradation
View Patent ↗A solid oxide fuel cell (SOFC) includes a cathode electrode, a solid oxide electrolyte, and an anode electrode. The electrolyte and/or electrode composition includes zirconia stabilized with (i) scandia, (ii) ceria, and (iii) at least one of yttria and ytterbia. The composition does not experience a degradation of ionic conductivity of greater than 15% after 4000 hrs at a temperature of 850° C.
1. A scandia stabilized zirconia electrolyte composition for a solid oxide fuel cell, comprising a formula (ZrO 2 ) 1-w-x-a-b (Sc 2 O 3 ) w (CeO 2 ) x (Y 2 O 3 ) a (Yb 2 O 3 ) b , where 0.09≦w≦0.11; 0<x≦0.025; a+b=z; 0≦z≦0.025; and x+z≧0.02, wherein:
w=0.1; x=0.01; and z=0.01; and
the composition comprises zirconia containing 10 mol % Sc 2 O 3 , 1 mol % CeO 2 and 1 mol % Y 2 O 3 .
2. The electrolyte composition of claim 1 , wherein:
the composition does not experience a degradation of ionic conductivity of greater than 15% after 4000 hrs and at a temperature of 850° C.;
the composition comprises a cubic phase which substantially lacks tetragonal phase domains after operating in a solid oxide fuel cell at 850° C. for at least 4000 hours in at least one of air or hydrogen ambient; and
the composition does not experience a cubic to rhombohedral phase transition at a temperature of about 25 to 850° C.
3. The composition of claim 1 , wherein the composition is utilized as an electrolyte layer of a planar solid oxide fuel cell comprising an anode and a cathode, and the electrolyte layer supports the anode and cathode.