Non-aqueous composition comprising partially fluorinated methacrylic polymers
View Patent ↗A solvent-based non-aqueous fluorinated methacrylate polymer comprising repeating units in any sequence from (1) at least one fluorinated methacrylate, and (2) at least one non-fluorinated alkyl acrylate and (3) at least one non-fluorinated hydroxyalkyl methacrylate, provided that a) the repeating unit of fluorinated methacrylate is present in a range of about 40%-80% by weight of total monomers added, b) the repeating unit of non-fluorinated alkyl acrylate is present in a range of about 10%-35% by weight of total monomers added, and c) the repeating unit of non-fluorinated hydroxyalkyl methacrylate is present in a range of about 5%-25% by weight of total monomers added, and d) the total of all repeating units is 100% by weight.
1. A fluorinated methacrylate polymer composition comprising repeating units in any sequence from (1) at least one fluorinated methacrylate, and (2) at least one non-fluorinated alkyl acrylate and (3) at least one non-fluorinated hydroxyalkyl methacrylate,
provided that
a) the repeating unit of fluorinated methacrylate is present in a range of from 40% to 80% by weight of total monomers added,
b) the repeating unit of non-fluorinated alkyl acrylate is present in a range of from 10% to 35% by weight of total monomers added, and
c) the repeating unit of non-fluorinated hydroxyalkyl methacrylate is present in a range of from 5% to 25% by weight of total monomers added, and
d) the total of all repeating units is 100% by weight;
wherein the fluorinated methacrylate is:
CF 3 (CF 2 ) 5 —CH 2 CH 2 —OC(O)—C(CH 3 )═CH 2 , the non-fluorinated alkyl acrylate is stearyl acrylate, the non-fluorinated hydroxyalkyl methacrylate is 2-hydroxyethyl methacrylate, and
the fluorinated methacrylate polymer composition is solvent-based and non-aqueous.
2. A method for treating a leather substrate comprising contacting the leather substrate with a solvent-based fluorinated methacrylate polymer to provide water and oil repellency, wherein the fluorinated methacrylate polymer comprises repeating units in any sequence from (1) at least one fluorinated methacrylate, and (2) at least one non-fluorinated alkyl acrylate and (3) at least one non-fluorinated hydroxyalkyl methacrylate,
provided that
a) the repeating unit of fluorinated methacrylate is present in a range of from 40% to 80% by weight of total monomers added,
b) the repeating unit of non-fluorinated alkyl acrylate is present in a range of from 10% to 35% by weight of total monomers added, and
c) the repeating unit of non-fluorinated hydroxyalkyl methacrylate is present in a range of from 5% to 25% by weight of total monomers added, and
d) the total of all repeating units is 100% by weight;
wherein the fluorinated methacrylate is CF 3 (CF 2 ) 5 —CH 2 CH 2 —OC(O)—C(CH 3 )═CH 2 , the non-fluorinated alkyl acrylate is stearyl acrylate the non-fluorinated hydroxyalkyl methacrylate is 2-hydroxyethyl methacrylate, and the fluorinated methacrylate polymer composition is solvent-based and non-aqueous.
3. The method of claim 2 wherein the contacting is by spray, dipping, foam, nip, immersion, brush, roller, sponge, or mat techniques.
4. The method of claim 2 wherein the contacting is by spray, dipping, or brush techniques.
5. A method for treating a hard surface substrate comprises contacting the hard surface substrate with a solvent-based fluorinated methacrylate polymer to provide water repellency, oil repellency, and stain resistance wherein the fluorinated methacrylate polymer comprises repeating units in any sequence from (1) at least one fluorinated methacrylate, and (2) at least one non-fluorinated alkyl acrylate and (3) at least one non-fluorinated hydroxyalkyl methacrylate,
provided that
a) the repeating unit of fluorinated methacrylate is present in a range of from 40% to 80% by weight of total monomers added,
b) the repeating unit of non-fluorinated alkyl acrylate is present in a range of from 10% to 35% by weight of total monomers added, and
c) the repeating unit of non-fluorinated hydroxyalkyl methacrylate is present in a range of from 5% to 25% by weight of total monomers added, and
d) the total of all repeating units is 100% by weight
wherein the fluorinated methacrylate is CF 3 (CF 2 ) 5 —CH 2 CH 2 —OC(O)—C(CH 3 )═CH 2 , the non-fluorinated alkyl acrylate is stearyl acrylate, the non-fluorinated hydroxyalkyl methacrylate is 2-hydroxyethyl methacrylate, and the fluorinated methacrylate polymer composition is solvent-based and non-aqueous.
6. The method of claim 5 wherein the contacting is by brush, spray, roller, doctor blade, wipe or dip techniques.
7. The method of claim 5 wherein the contacting is by spray or wet-on-wet techniques.
8. The method of claim 5 wherein the hard surface substrate is unglazed concrete, brick, tile, stone, granite, limestone, grout, mortar, composite materials, terrazzo, gypsum board, marble, statuary, monuments, or wood.