Method for surface treating a heat exchanger, hydrophilizing treatment agent, and aluminum heat exchanger
View Patent ↗A method for surface treating a heat exchanger, a hydrophilizing treatment agent used in this method, and an aluminum heat exchanger obtained from this method are provided that excel in the initial adherence, hydrophilicity, and odor suppressibility, and can maintain these abilities for an extended time, while having little burden on the environment and the human body. The method for surface treating an aluminum heat exchanger that is brazed includes (1) a pickling treatment step; (2) a chemical conversion treatment step; and (3) a hydrophilization treatment step, in which the acidic cleaning agent contains nitric acid and sulfuric acid and contains ferric salt in a predetermined amount, the hydrophilizing treatment agent contains silica grains coated with a vinyl alcohol polymer and a polyallylamine resin.
1. A method for surface treating a heat exchanger, comprising:
(1) a pickling treatment step of causing an acidic cleaning agent to come into contact with a heat exchanger made of an aluminum material and vacuum brazed;
(2) A chemical conversion treatment step of causing a zirconium-based chemical conversion treatment agent to come into contact with the aluminum material after the pickling treatment step; and
(3) a hydrophilization treatment step of causing a hydrophilizing treatment agent to come into contact with the aluminum material after the chemical conversion treatment step,
wherein the acidic cleaning agent contains nitric acid and sulfuric acid, and contains 0.01 to 5% by mass of a ferric salt, and
wherein the hydrophilizing treatment agent contains silica grains coated by a vinyl alcohol polymer, and a polyallylamine resin, a total content of the silica grains and vinyl alcohol polymer being in the range of 0.2 to 25% by mass, a mass ratio of silica grains to vinyl alcohol polymer being in the range of 30:70 to 70:30, and a content of the polyallylamine resin being the range of 100 ppm to 5000 ppm.
2. The method according to claim 1 , wherein the ferric salt is at least one selected from the group consisting of iron sulfate, iron nitrate, iron acetate, and iron chloride.
3. The method according to claim 1 , wherein the heat exchanger is an evaporator for a vehicle air-conditioner.