Provided in one embodiment is an implantable support material for culturing cells, wherein at least some of the cells substantially maintain at least one of (i) phenotype and (ii) genotype thereof after being cultured on the support material.
1 . An implantable support material for culturing cells and that is capable of maintaining and transporting viable cell sheets,
wherein at least some of the cells substantially maintain at least one of (i) phenotype and (ii) genotype thereof after being cultured on the support material.
2 . The implantable support material of claim 1 , wherein the support material comprises microbial cellulose.
3 . The implantable support material of claim 1 , wherein the support material comprises oxidized microbial cellulose.
4 . The implantable support material of claim 1 , wherein the cells are mammalian cells.
5 . The implantable support material of claim 1 , wherein the cells are chondrocytes, synovial cells, epithelial cells, retinal pigment cells or combinations thereof.
6 . The implantable support material of claim 1 , wherein at least some of the cultured cells form at least partial confluence.
7 . The implantable support material of claim 1 , wherein at least some of the cultured cells form a cell sheet.
8 . The implantable support material of claim 1 , wherein the support material has a white light transmittance of at least about 80%.
9 . The implantable support material of claim 1 , wherein the support material has a thickness of less than about 60 microns.
10 . The implantable support material of claim 1 , wherein the support material has a tensile strength of at least about 1.5 MPa.
11 . The implantable support material of claim 1 , wherein the support material has an elongation at break of at least about 60%.
12 . The implantable support material of claim 1 , wherein the support material has a conformability of at least 88°.
13 . The implantable support material of claim 1 , wherein at least some of the cells form a cell sheet over the support material.
14 . A method of forming an implantable microbial cellulose support material for culturing cells, comprising:
(i) providing a microbial cellulose material, which has been fermented in a bioreactor for less than about 5 days;
(ii) cleaning the microbial cellulose material; and
(iii) pressing mechanically the microbial cellulose material, whereby the implantable microbial cellulose support material is formed.
15 . The method of claim 14 , wherein the cleaning in step (ii) further comprises treating the microbial cellulose material with a sodium hydroxide solution.
16 . The method of claim 14 , wherein the microbial cellulose material is made by Acetobacter Xylinum.
17 . The method of claim 14 , further comprising packaging the implantable biocellulose support material after step (iii).
18 . The method of claim 14 , wherein the microbial cellulose material comprises oxidized microbial cellulose.
19 . An implant material to be implanted into a subject in need thereof, the material comprising:
(i) a microbial cellulose support material with adequate strength for the transfer of the cells and to be sutured in place; and
(ii) a cell sheet disposed on the support material.
20 . The implant material of claim 19 , wherein the implant is for cornea repair, cartilage repair, connective tissue repair, heart tissue repair, ligament repair, dura tissue repair, or a combination thereof.
21 . The implant material of claim 19 , wherein the support material has a conformability of at least 88°.
22 . The implant material of claim 19 , wherein the support material has a white light transmittance of at least 80%.
23 . The implantable material of claim 19 , wherein substantially all of the cells in the cell sheet are viable.
24 . The implantable material of claim 19 , wherein the microbial cellulose material comprises oxidized microbial cellulose.