Lithium ion battery
View Patent ↗An object of the present invention is to provide a lithium ion battery which is excellent in properties at large current and can be applied to applications requiring high output power even when the mixture layers are made thick. The present invention provides a lithium ion battery including a positive electrode including a positive electrode mixture layer formed on a current collector, a negative electrode including a negative electrode mixture layer formed on a current collector and an electrolyte, the positive electrode and the negative electrode being disposed through the intermediary of a separator, wherein the positive electrode includes as a positive electrode active material a lithium composite oxide represented by LiNi a Mn b CO c M d O 2 (in the formula, M is at least one selected from the group consisting of Fe, V, Ti, Cu, Al, Sn, Zn, Mg, B and W, a+b+c+d=1, 0.2≦a≦0.8, 0.1≦b≦0.4, 0≦c≦0.4 and 0≦d≦0.1), the negative electrode includes graphite as a negative electrode active material, the interlayer distance (d 002 ) of the graphite is 0.335 nm or more and 0.338 nm or less, the one-side thickness A (μm) of the positive electrode mixture layer is 60 or more and 85 or less, the product A×B between the one-side thickness A and the density B (g/cm 3 ) of the positive electrode mixture layer is 160 or more and 220 or less, the one-side thickness C (μm) of the negative electrode mixture layer is 40 or more and 75 or less, and the product C×D between the one-side thickness C and the density D (g/cm 3 ) of the negative electrode mixture layer is 65 or more and 105 or less.
1. A lithium ion battery comprising a positive electrode including a positive electrode mixture layer formed on a current collector, a negative electrode including a negative electrode mixture layer formed on a current collector and a liquid electrolyte, the positive electrode and the negative electrode being disposed through the intermediary of a separator,
wherein the positive electrode comprises as a positive electrode active material a lithium composite oxide represented by LiNi a Mn b Co c M d O 2 , wherein in the formula, M is at least one selected from the group consisting of Fe, V, Ti, Cu, Al, Sn, Zn, Mg, B and W, a+b+c+d=1, 0.2≦a≦0.8, 0.1≦b≦0.4, and 0≦d≦0.1,
an amount of the positive electrode active material in the positive electrode mixture layer is 79 wt % or more and 94 wt % or less,
the negative electrode comprises graphite as a negative electrode active material,
an amount of the negative electrode active material in the negative electrode mixture layer is 85 wt % or more and 99 wt % or less,
the interlayer distance (d 002 ) of the graphite is 0.335 nm or more and 0.338 nm or less,
the one-side thickness A (μm) of the positive electrode mixture layer is 60 or more and 85 or less,
the product A×B between the one-side thickness A and the density B (g/cm 3 ) of the positive electrode mixture layer is 160 μm·g/cm 3 or more and 220 μm·g/cm 3 or less,
the one-side thickness C (μm) of the negative electrode mixture layer is 40 or more and 75 or less, and
the product C×D between the one-side thickness C and the density D (g/cm 3 ) of the negative electrode mixture layer is 65 μm·g/cm 3 or more and 105 μm·g/cm 3 or less.
2. The lithium ion battery according to claim 1 , wherein (A×B)/(C×D) is 2.0 or more and 2.3 or less.
3. The lithium ion battery according to claim 2 , wherein at least one of the positive electrode mixture layer and the negative electrode mixture layer further comprises carbon fiber.
4. The lithium ion battery according to claim 2 , wherein the pores possessed by the graphite are such that when the volume of the pores having a pore diameter of 1 nm or more and less than 5 nm is represented by V 1 and the volume of the pores having a pore diameter of 5 nm or more and less than 100 nm is represented by V 2 , V 1 /V 2 is 0.01 or more and 0.10 or less.
5. The lithium ion battery according to claim 2 , wherein the interlayer distance (d 002 ) of the graphite is 0.336 nm or more and 0.337 nm or less.