View Patent ↗A low emissivity and EMI shielding transparent composite film typically for use in association with window glazing and comprising a transparent film substrate having on one side thereof an underlayer of abrasion resistant hardcoat material with at least one infrared reflective layer covering the underlayer, typically a metallic layer which may be encased in metal oxide layers, which is then covered with a thin external protective top coat of a cured fluorinated resin.
1. A low emissivity transparent composite film comprising:
a transparent film substrate;
an underlayer of abrasion resistant hardcoat material deposited on the surface of the film substrate and comprising a crosslinked acrylate polymer and metal oxide nanoparticles, the underlayer having a dried thickness of about 2 to about 6 microns;
at least one infrared reflective layer; and
a transparent, protective top coat disposed over the infrared reflective layer, the protective top coat having a thickness of less than 0.5 microns and comprising a polysilazane, fluoro silane, fluoroalkyl silane, or combination thereof;
wherein the composite film has an emissivity of less than about 0.30.
2. The composite film of claim 1 wherein the infrared reflecting layer comprises at least one metallic layer selected from the group consisting of aluminum, copper, gold, nickel, silver, platinum, palladium, tungsten, titanium, and alloys thereof.
3. The composite film of claim 2 wherein the infrared reflective layer comprises at least one spacer layer comprising a transparent conductive layer, a dielectric layer, or combinations thereof.
4. The composite film of claim 3 wherein the spacer layer comprises at least one metal oxide selected from the group consisting of indium oxide, indium zinc oxide, and indium tin oxide.
5. The composite film of claim 1 , wherein the underlayer has an abrasion delta haze of 5 percent or less.
6. The composite film of claim 1 wherein the infrared reflective layer comprises at least one thin metal film capable of protecting the infrared reflective layer.
7. The composite film of claim 6 wherein the thin metal film comprises at least one metal selected from the group consisting of nickel, chromium, nobium, platinum, cobalt, zinc, molybdenum, zirconium, vanadium and alloys thereof.
8. The composite film of claim 7 wherein the thin metal film comprises a nickel-chromium alloy.
9. The composite film of claim 1 wherein the infrared reflective layer comprises a plurality of thin spacer layers disposed between a plurality of transparent conductive layers.
10. A low emissivity transparent composite film comprising:
a transparent polyester film substrate;
an underlayer of abrasion resistant hardcoat material deposited on the surface of the film substrate and comprising a crosslinked acrylate polymer and about 21 to about 65 weight percent of metal oxide nanoparticles, the underlayer having a dried thickness of about 2 to about 6 microns and an abrasion delta haze of about 3 to about 5%;
at least one infrared reflective layer; and
a transparent, protective top coat disposed over the infrared reflective layer, the protective top coat having a thickness of less than about 0.5 microns and comprising a polysilazane, fluoro silane, fluoroalkyl silane, or combination thereof;
wherein the composite film has an emissivity of less than about 0.25.
11. The composite film of claim 10 which has an emissivity of less than about 0.20.
12. The composite film of claim 11 which has a visible light transmission of up to about 75 percent.
13. The composite film of claim 10 which has an emissivity of less than about 0.10.
14. The composite film of claim 13 which has a visible light transmission of about 28 percent to about 47 percent.
15. The composite film of claim 13 which has a visible light transmission up to about 70 percent.
16. The composite film of claim 10 wherein the metal oxide nanoparticles comprise silicon dioxide, aluminum oxide, or a combination thereof.
17. The composite film of claim 10 wherein the infrared reflecting layer comprises at least one metallic layer selected from the group consisting of aluminum, copper, gold, nickel, silver, platinum, palladium, tungsten, titanium, and alloys thereof.
18. A method of manufacturing the low emissivity transparent composite film of claim 1 , comprising:
coating a mixture of an abrasion resistant hardcoat material comprising a polyacrylate polymer and metal oxide nanoparticles to one side of a transparent film substrate;
curing the coated side of the film substrate to form an underlayer having a dried thickness of about 2 to about 6 microns;
sputtering an infrared reflecting layer on the underlayer; and
applying a transparent, protective top coat over the infrared reflective layer, the protective top coat having a thickness of less than 0.5 microns and comprising a polysilazane, fluoro silane, fluoroalkyl silane, or combination thereof;
wherein the composite film has an emissivity of less than about 0.30.